Abstract:A new zirconium oxide-based media for arsenate removal from water was fabricated and evaluated in batch and continuous flow experiments. Highly porous (epsilonp approximately 0.9) nanostructured zirconium oxide spheres were fabricated by the impregnation of macroporous ion-exchange media (CalRes 2103, Calgon) with zirconium salt; the media was then ashed at T > 750 +/- 50 degrees C to remove the organic polymer resin and obtain ZrO2 spheres. The spheres generally ranged from 200 to 800 microm in diameter, and consisted of ZrO2 nanoastructures generally ranging between 20 and 100 nm. They also exhibited monoclinic and tetragonal crystalline structures, and had an isoelectric point of 5.6. Equilibrium batch experiments were conducted in 10 mM NaHCO3 buffered nanopure water at three pH values (6.4,7.3, and 8.3) with 120 microg/L As(V). Data were fit with the Freundlich isotherm equation (q(e) = Kx CE(1/n)), resulting in an intensity parameter (1/n) of approximately 0.33 and capacity parameters (K) ranging from 115 to 400 (microg As(V) g(-1) dry media)(L microg(-1))1/n. The pore diffusion coefficient and toruosity were estimated to be 6.4 x 10(-6) cm2 s(-1) and 1.3, respectively. For a packed bed adsorbent operating at a loading rate of 11.5 m3 m(-2) hr(-1) in a realistic continuous flow experiment, the external mass transport coefficient was estimated to be kf approximately 6.3 x 10(-3) cm s(-1). The pore diffusion coefficient and the external mass transport coefficient were used with the pore surface diffusion model (PSDM) to predict the arsenate breakthrough curve. A short bed adsorbent (SBA) test was conducted under the same conditions to validate the model. In this study, surface diffusion was ignored because the particles have a very high porosity. The validated model was used to predict arsenate breakthrough in a simulated full-scale system. The overall combined use of modeling, material characterization, equilibria, and kinetics tests determined the suitability of the media for arsenate treatment cheaper, easier, faster, and with less media than a long duration pilot test would have. Although the fabricated zirconium oxide spheres exhibited adsorption capacity comparable to some commercially available media such as iron based (hydr)oxides, the high cost of fabrication may render the media not feasible for wide use in commercial applications. However, the very high porosity of this media provides for improved pore diffusion and faster overall mass transport, which may be critical for applications where mass transport is the limiting factor.

Acid and organic resistant nano-hydrated zirconium oxide (HZO)/polystyrene hybrid adsorbent for arsenic removal from water

Nanoconfinement boosts affinity of hydrated zirconium oxides to arsenate: Surface complexation modeling study.

Enhanced Removal of Arsenic from Water by Using Sub-10 Nm Hydrated Zirconium Oxides Confined Inside Gel-Type Anion Exchanger.

Preferable removal of phosphate from water using hydrous zirconium oxide-based nanocomposite of high stability.

Arsenate removal from underground water by polystyrene-confined hydrated ferric oxide (HFO) nanoparticles:effect of humic acid

Enhanced Removal of Fluoride by Polystyrene Anion Exchanger Supported Hydrous Zirconium Oxide Nanoparticles.

A Gel Resin-supported Nano-hydrated Iron Oxide for Arsenate Sorption from Water

Superior removal of arsenic from water with zirconium metal-organic framework UiO-66

Enhanced Water Decontamination from Methylated Arsenic by Utilizing Ultra-Small Hydrated Zirconium Oxides Encapsulated Inside Gel-Type Anion Exchanger

Arsenate removal by nanostructured ZrO2 spheres

Arsenate Removal from Aqueous Media by Nanosized Hydrated Ferric Oxide (HFO)-Loaded Polymeric Sorbents: Effect of HFO Loadings

Arsenic Captured from Drinking Water with Fe-Zr Adsorbents

Effective Removal of Heavy Metals by Nanosized Hydrous Zirconia Composite Hydrogel and Adsorption Behavior Study

Enhanced arsenite removal from water using zirconium-ferrocene MOFs coupled with peroxymonosulfate:oxidation and multi-sites adsorption mechanism

Selective and Efficient Removal of As(V) and As(III) from Water by Resin-Based Hydrated Iron Oxide

Solid Brønsted Acidity Boosts Adsorption Reactivity of Nano-Adsorbent for Water Decontamination

COMPARATIVE STUDY OF ARSENITE REMOVAL FROM WATER BY POLYMER-SUPPORTED HYDRATED METALLIC OXIDES

Preparation of Polymer-Supported Hydrated Ferric Oxide Based on Donnan Membrane Effect and Its Application for Arsenic Removal

Zr-doped MIL-101(Fe)/Graphene oxide nanocomposites: An efficient and water-stable MOF-based adsorbent for As(V) adsorption in aqueous solution

Surface chemistry of polymer-supported nano-hydrated ferric oxide for arsenic removal: effect of host pore structure

Highly Efficient Removal of Arsenite from Water by Using Renewable Sub-5 Nm Zr-Mn Binary Oxides Confined Inside Gel-Type Ion Exchanger