Abstract:The oxidation behavior of a nickel-based superalloy GH738 was studied by isothermal oxidation tests in still air at different temperatures, with exposure time up to 100 h. Oxidation-kinetic curves were plotted using the mass gain method. The surface and cross-sectional morphologies were observed by scanning electron microscopy (SEM). A composition analysis and an oxidation-product identification were conducted using energy-dispersive X-ray spectroscopy (EDS) and an X-ray diffraction (XRD), respectively. The results showed that GH738 exhibited parabolic oxidation-kinetic curves, with stable parabolic-rate constants at each temperatures. The activation energy of oxide growth was calculated to be 329.6 kJ·mol−1. Cr2O3 (chromia) was the external oxidation product at 800 °C. A TiO2–Cr2O3 double-layer structure was formed at 900 °C. The position of TiO2 changed from the oxide–metal interface to the air–oxide interface by the diffusion of Ti atoms in chromia during the oxidation time at this temperature. Spallation was observed in the Cr0.12Ti0.78O1.74–Cr2O3 multi-layer oxide of at 1000 °C, which increased the oxidation rate. For all the tests, the main internal oxide was always Al2O3. The entire GH738 oxidation process was interpreted by the competitive diffusion of elements (Cr, Ti, Ni, etc.) in metal matrix and chromia, while a schematic diagram of oxidation process was proposed.<h3 class="a-plus-plus">Graphic abstract</h3>

Oxidation behaviours of electron beam physical vapour deposition fabricated microcrystalline Ni–23·5Cr–2·66Co–1·44Al superalloy sheet at 1000°C

Oxidation Kinetics of Microcrystalline Ni–11.5Cr–4.5Co–0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 900 °C

Oxidation Behaviors of NiCrCoAl Superalloy Sheet Prepared by EB-PVD at 1000℃

Oxidation Kinetics of Microcrystalline Ni-11.5Cr-4.5Co-0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 800 °C

Cyclic oxidation behaviour of as-deposited Ni-11·5Cr-4·5Co-0·5Al superalloy sheet when heated at 800°C

Oxidation Kinetics Of Microcrystalline Ni-11.5cr-4.5co-0.5a1 Superalloy Sheet Fabricated By Electron Beam Physical Vapor Deposition At 800 Degrees C

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

The Isothermal Oxidation Behaviors of As-Deposited and Heat-Treated Ni–11.5Cr–4.5Co–0.5Al Sheet by EB-PVD at 800°C

Oxidation behavior at 1000 circle C for nanocrystalline Ni-20Cr-0.6Al alloy deposited by EB-PVD

Microstructural evolution during exposure in air and oxidation behavior of a nickel-based superalloy

ISOTHERMAL OXIDATION BEHAVIOR OF A SINGLE CRYSTAL NICKEL-BASED SUPERALLOY

Oxidation behavior of a nickel-based single crystal superalloy at 1100 °C under different oxygen concentration

Oxidation Behaviour of Sputter-Depositedni–cr–al Micro-Crystalline Coatings

Isothermal Oxidation Resistance of As-cast NiAl and NiAl-(Cr, Mo) Eutectic Alloys at 1000°C

Oxidation Behaviour of Microcrystalline Ni-Cr-Al Alloy Coatings at 900°C

Mechanical Properties and Oxidation Formation of Eb-Pvd Deposited Ni-Cr-Al Alloy

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

Microstructure Evolution of Electron Beam Physical Vapour Deposited Ni-23.5Cr-2.66Co-1.44Al Superalloy Sheet During Annealing at 600 °C

Oxidation behavior of Ni-based superalloy GH738 in static air between 800 and 1000 °C

Anisothermal Oxidation of Micro-Crystalline Ni-20Cr-5Al Alloy Coating at 850-1280°C

Oxidation Behavior of a New Fe–Ni–Cr-based Alloy in Pure Steam at 750 °C