Abstract:The evolution of phase composition and mechanical properties and the formation of oxide layers on Fe40–xNiCoCrAlx (x = 5 and 10 at.%) alloys in long-term oxidation at 900 and 1000°C were studied. In the initial cast state, depending on the aluminum content and valence electron concentration, the alloys contain only an fcc solid solution (VEC = 8 e/a) or a mixture of fcc and bcc phases (VEC = = 7.75 e/a). Thin continuous oxide scales containing Cr2O3 and NiCr2O4 spinel formed on the surface of both alloys oxidized at 900°C for 50 h. A further increase in the annealing time to 100 h leads to the formation of aluminum oxide Al2O3 in the scale on the Fe30Ni25Co15Cr20Al10 alloy, having high protective properties. An increase in the oxidation temperature to 1000°C results in partial failure of the protective layer on the alloy with 10 at.% Al. Long-term holding at 900°C (100 h) + 1000°C (50 h) does not change the phase composition of the Fe35Ni25Co15Cr20Al5 alloy matrix, being indicative of its high thermal stability. In the two-phase Fe30Ni25Co15Cr20Al10 alloy, the quantitative ratio of solid solutions sharply changes: the amount of the bcc phase increases from 4 to 54 wt.% and its B2-type ordering is observed. The mechanical characteristics of the starting alloys and those after long-term high-temperature annealing were determined by automated indentation. The hardness (HIT) and elastic modulus (E) of the cast Fe35Ni25Co15Cr20Al5 alloy are equal to 2 and 147 GPa, respectively, and decrease to 1.8 and 106 GPa after a series of long-term annealing operations. The Fe30Ni25Co15Cr20Al10 alloy shows the opposite dependence: HIT increases from 2.5 in the initial state to 3.1 GPa after annealing and E decreases from 152 to 134 GPa. This indicates that the Fe30Ni25Co15Cr20Al10 alloy is promising as a high-temperature oxidation-resistant and creep-resistant material.

The Isothermal Oxidation Behaviors of As-Deposited and Heat-Treated Ni–11.5Cr–4.5Co–0.5Al Sheet by EB-PVD at 800°C

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Oxidation Behaviors of NiCrCoAl Superalloy Sheet Prepared by EB-PVD at 1000℃

Oxidation Kinetics of Microcrystalline Ni–11.5Cr–4.5Co–0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 900 °C

Oxidation behaviours of electron beam physical vapour deposition fabricated microcrystalline Ni–23·5Cr–2·66Co–1·44Al superalloy sheet at 1000°C

Cyclic oxidation behaviour of as-deposited Ni-11·5Cr-4·5Co-0·5Al superalloy sheet when heated at 800°C

Oxidation Kinetics of Microcrystalline Ni-11.5Cr-4.5Co-0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 800 °C

Oxidation Kinetics Of Microcrystalline Ni-11.5cr-4.5co-0.5a1 Superalloy Sheet Fabricated By Electron Beam Physical Vapor Deposition At 800 Degrees C

Microstructure Evolution of Electron Beam Physical Vapour Deposited Ni-23.5Cr-2.66Co-1.44Al Superalloy Sheet During Annealing at 600 °C

Mechanical Properties and Oxidation Formation of Eb-Pvd Deposited Ni-Cr-Al Alloy

Study on the Microstructure of Nicocral Sheet Deposited by Eb-Pvd at 800 Degrees C

Oxidation behavior at 1000 circle C for nanocrystalline Ni-20Cr-0.6Al alloy deposited by EB-PVD

Isothermal Oxidation Behaviour of 800H Nickel-Based Alloy

Anisothermal Oxidation of Micro-Crystalline Ni-20Cr-5Al Alloy Coating at 850-1280°C

Oxidation behavior at 1100 °C of NiCrAlY coatings deposited by various PVD techniques

Oxidation Behavior of a New Fe–Ni–Cr-based Alloy in Pure Steam at 750 °C

High Temperature Oxidation Behavior of Al0.5CrCoFeNi High Entropy Alloy

Structural State of High-Entropy Fe40–xNiCoCrAlx Alloys in High-Temperature Oxidation

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

Research on Microstructure of Ni-20.3Cr-4.6Co-2.1Al As-deposited State Sheet Prepared by EB-PVD

Oxidation behavior of 4774DD1 Ni-based single-crystal superalloy at 980 °C in air