Abstract:Calcium aluminate phases have a particular effect on the early heat release during setting initiation and have a substantial influence on the further workability of ordinary Portland cement. The nature of the calcium aluminate hydration products and its kinetics strongly depends on sulfate content and humidity. The effect of mineralisers on melt formation and viscosity is well described for calcium silicate systems, but information is still lacking for calcium aluminates. Therefore, the synergistic effect on the crystal structure and hydration mechanism of the tricalcium aluminate phase of the addition of mineralizers, i.e. Li 2 O, CuO, SO 3 to the raw meal is here investigated. Co-doped calcium aluminate structures were formed during high-temperature treatment. Thermal analysis (TG–DTA and heating microscopy) was used to describe the ongoing high-temperature reaction. Resulting phase composition was dependent on the concentration of the mineralizer. While phase pure system was prepared with low mineralizer concentrations, with increasing mineralizer content the secondary phases were formed. Raman spectroscopy and XPS analysis were used to investigate the cation substitution and to help describe the cations bonding in co-doped calcium aluminate system. Prepared powders have been hydrated in a controlled manner at different temperatures (288, 298, 308 K). The resulting calorimetric data have been used to investigate the hydration kinetics and determine the rate constant of hydration reaction. First-order reaction (FOR) model was here applied for the activation energy and frequency factor calculations. The metastable and stable calcium aluminate hydrates were formed according to initial phase composition. In phase pure systems with low S content, the formation of stable and metastable hydrates was depended on the reaction temperature. Conversely, in systems with secondary phases and higher S content, the hydration mechanism resembled that which appears in calcium sulfoaluminates.

Hydration Kinetics Process of Low Alkalinity Sulphoaluminate Cement and Its Thermodynamical Properties

Effect of Alkali Content in Cement on Its Hydration Kinetics and Mechanical Properties

Hydration kinetics of C3A: effect of lithium, copper and sulfur-based mineralizers

Role of the structure of synthetic Al(OH)3 on the properties of sulfoaluminate cement-based materials

Advances in understanding cement hydration mechanisms

A New Hydration Kinetic Model Based on Boundary Nucleation and Growth Mechanism with Time-Dependent Growth Rate: Application to Quantitively Characterize the Influence of Alkali on the Early Hydration of Cement

Investigation on the Unusual Hydration and Hardening Process of a Portland Cement with Low Alkali Sulfate Content

Influence of water to cement ratio and lithium carbonate on sulphoaluminate cement hydration process

Kinetic study on the hydration of supersulfated cements

Hydration kinetics of aluminate cement containing magnesium aluminate spinel

Chloride binding behaviors and early age hydration of tricalcium aluminate in chloride-containing solutions

The influence of low calcium sulfate contents on early calcium aluminate cement–calcite hydration kinetics and pore solution chemistry

Insights into the effect mechanism of nano LiAl-LDHs on the early hydration of sulphoaluminate cement-based materials

Synthesis of alite, belite and ferrite in both monophase and polyphase states and their hydration behavior

The Early Hydration of OPC Investigated by In-Situ XRD, Heat Flow Calorimetry, Pore Water Analysis and 1H NMR: Learning about Adsorbed Ions from a Complete Mass Balance Approach

Research on the Hydration Properties of C4A3S-CSH2 Cement System at Different Temperatures

The influence of sulfate addition on hydration kinetics and C-S-H morphology of C3S and C3S/C3A systems

Hydration kinetics of cation exchanged clinoptilolite zeolite based cementitious materials

Influence of Different Alkali Sulfates on the Shrinkage, Hydration, Pore Structure, Fractal Dimension and Microstructure of Low-Heat Portland Cement, Medium-Heat Portland Cement and Ordinary Portland Cement

Recent Development on Understanding Cement Hydration Mechanism and Effects of Chemical Admixtures on Cement Hydration

Hydration Mechanism and Leaching Behavior of Bauxite-Calcination-method Red Mud-Coal Gangue Based Cementitious Materials.