Modulated Anisotropic Growth of 2D SnSe Based on the Difference in a / b / c -Axis Edge Atomic Structures
Gonglei Shao,Xiong-Xiong Xue,Meiqing Yang,Junqiang Yang,Xiao Liu,Haozi Lu,Yubin Jiang,Yuanyuan Jin,Quan Yuan,Jian Sun,Huimin Li,Guo Hong,Xuli Chen,Yexin Feng,Song Liu
DOI: https://doi.org/10.1021/acs.chemmater.1c01147
IF: 10.508
2021-05-21
Chemistry of Materials
Abstract:The controlled anisotropic growth of two-dimensional (2D) materials along a specific crystal axis is very crucial to explore the axis-dependent performance, which derives from the difference of atom arrangement in different crystal axes, while the relevant research is still insufficient. Here, we demonstrated a systematic investigation on the controllable anisotropic growth of 2D SnSe along different axis directions from both the experimental and theoretical perspectives. The anisotropy growth of 2D SnSe was attributed to the difference in atomic structures and bonding features between the zigzag edge (along the <i>b</i>-axis) and armchair edge (along the <i>c</i>-axis), as well as the chemical inertness of the base plane in the <i>a</i>-axis. Scanning transmission electron microscopy (STEM) images further verified that the long side of rectangular 2D SnSe is an armchair edge and the short side is a zigzag edge. The growth rates along the <i>b</i>- and <i>c</i>-axes could be effectively adjusted by hydrogen, attributed to the difference in desorption energy between hydrogen and different edge structures. The higher hydrogen concentration led to a shorter <i>b</i>-axis and a longer <i>c</i>-axis. The morphologies of 2D SnSe could be regulated in the range from square nanosheets to linear nanowires. In terms of the <i>a</i>-axis, 2D SnSe was precisely limited to a minimum value of 7.42 nm <i>via</i> a one-step rapid cooling method and could be further thinned to a bilayer using a two-step method with an additional annealing etching step. This study has demonstrated a facile strategy toward the structure-dependent controllable growth of 2D anisotropic materials, which shed new light on the orientation judgment and axis-dependent mechanism of the crystal axis of anisotropic materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.1c01147?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.1c01147</a>.Basic characterization of 2D SnSe by normal growth, morphological evolution of 2D SnSe with increased H<sub>2</sub> flow, DFT calculations for different binding energies of H<sub>2</sub> at different edges, and thickness evolution of SnSe by annealing and fast cooling (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c01147/suppl_file/cm1c01147_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical