Abstract:A corn stalk cellulose-based adsorbent was reasonably designed and synthesized by two steps of modification to effectively remove Cd(II) and Ni(II) from wastewater of nickel–cadmium (Ni–Cd) and nickel-metal hydride (Ni-MH) batteries. Glycidyl methacrylate (GMA), N,N-methylene-bis- acrylamide (MBA), and potassium persulfate (KSP) was selected as the grafting monomer, cross-linking agent and initiator, respectively, in the first step to introduce enough epoxy groups and generate three dimensional (3D) network structures on the cellulose (Cell) surface. Under the optimum conditions of weight ratio of GMA: Cell = 3:1, 20 mmol L–1 KSP, 5.0 wt.% of MBA to Cell and 60°C for 2 h, the maximum grafting efficiency and the amount of epoxy groups could reach 93.69% and 4.96 mmol g–1, respectively. Then this grafted and cross-linked product (Cell-g-GMA-c-MBA) was further reacted with diethylenetriamine (DETA) to introduce amino groups on the adsorbent. The final adsorbent (Cell-g-GMA-c-MBA-DETA) with the maximum amount of 7.20 mmol g–1 amino groups was obtained under the optimized amination conditions. The experiment results showed that the maximum adsorption capacity of Cd(II) and Ni(II) on Cell-g-GMA-c-MBA-DETA could reach 367.3 and 295.9 mg g–1, respectively at 45°C and pH = 4.5. The detailed investigation on relationships between microstructures and adsorption performances of Cell-g-GMA-c-MBA-DETA proved that the introduced sufficient amino groups were the major adsorption sites to adsorb Cd(II) and Ni(II). Cd(II) was inclined to be adsorbed by forming chelation complexes with 2–3 mmol N atoms from amino groups while the adsorption of Ni(II) would require at least 1 mmol N atom from amino groups by accepting lone-pair electrons and forming coordinate bonds. This modified cellulose also displayed a good reproducibility, whose regeneration efficiency for adsorbing Cd(II) and Ni(II) after sixth cycles were still 80% and 82%, respectively. It could be considered as a promising material for effective removal of Cd(II) and Ni(II) from batteries wastewater.

Three-Dimensional Macroporous Cellulose-Based Bioadsorbents for Efficient Removal of Nickel Ions from Aqueous Solution

Modified Native Cellulose Fibers-A Novel Efficient Adsorbent For Both Fluoride And Arsenic

Ni(II) and Pb(II) Removal Using Bacterial Cellulose Membranes

Preparation of Cotton-Based Fibrous Adsorbents for the Removal of Heavy Metal Ions.

Reasonable design of a corn stalk cellulose-based adsorbent for adsorption of Cd(II) and Ni(II): adsorption behaviors and mechanisms

Three-dimensional macroscopic aminosilylated nanocellulose aerogels as sustainable bio-adsorbents for the effective removal of heavy metal ions

Continuous fixed‐bed column adsorption of nickel (II) using recyclable three‐dimensional cellulose nanocrystals‐hydrogel: Bed depth service time, Thomas, Adams–Bohart, and Yoon–Nelson modelling

A Novel Cellulose-Based Composite Hydrogel Microsphere Material: for Efficient Adsorption of Co(II) and Ni(II) Ions in Water

Preparation and Optimization of Polyaniline/ Titanium Dioxide/ Carboxymethyl Cellulose Powder for Effective Nickel Adsorption

Ultrafast removal of Ni(II) ions over a bio-based antibacterial adsorbent

All-biomass cellulose/casein adsorbent fabricated via the "green solvent system" of ionic liquid for the efficient removal of Cu(II), Cd(II) and Pb(II)

Two all-biomass cellulose/amino acid spherical nanoadsorbents based on a tri-aldehyde spherical nanocellulose II amino acid premodification platform for the efficient removal of Cr(VI) and Cu(II)

Recyclable magnetic nickel ferrite–carboxymethyl cellulose–sodium alginate bio-composite for efficient removal of nickel ion from water

Adsorption of heavy metal ions from aqueous solution by carboxylated cellulose nanocrystals

Fabrication of 3D compressible polyaniline/cellulose nanofiber aerogel for highly efficient removal of organic pollutants and its environmental-friendly regeneration by peroxydisulfate process

Efficient and Rapid Removal of Nickel Ions from Electroplating Wastewater Using Micro-/Nanostructured Biogenic Manganese Oxide Composite

Optimization and Adsorption Behavior of Nanostructured NiFe2O4/Poly AMPS Grafted Biopolymer

Nickel ion removal from aqueous solutions through the adsorption process: a review

Enhancing Removal of Cr(VI), Pb2+, and Cu2+ from Aqueous Solutions Using Amino-Functionalized Cellulose Nanocrystal

Highly selective adsorption of Hg (II) from aqueous solution by three-dimensional porous N-doped starch-based carbon

Anisotropic Nanocellulose Aerogel Loaded with Modified UiO-66 as Efficient Adsorbent for Heavy Metal Ions Removal