Abstract:Poly(L-lactide-co-epsilon-caprolactone) P(LLA-co-CL) copolymers with various L-lactide/epsilon-caprolactone(L-LA/epsilon-CL) mole ratios were prepared by the ring opening copolymerization of L-LA and epsilon-CL using nontoxic magnesium octoate as a catalyst in bulk. The time-conversion curves of L-LA and E-CL copolymerization were recorded by H-1-NMR. The results showed significantly more rapid polymerization of L-LA relative to E-CL. The carbonyl carbon signals in C-13-NMR are most sensitive to the sequence distributions of the lactidyl and caproyl units and used for calculating their average block length (L-LL(e) and L-C(e)). Two modes of transesterification occurred during the copolymerization process and played an important role in the redistribution of comonomer sequences. With polymerization progress, L-LL(e) decreased sharply and L-C(e) increased at first and then decreased gradually, as a result, the run number (R) increased gradually and the extent of randomness enhanced. The CLC sequence formed by the second mode of transesterification was observed at the end of reaction. Then, the reactivity ratios of L-LA and E-CL were measured to be r(LA) = 23 and r(CL) = 0.22, respectively, using the Fineman-Ross method. The results(r(LA) > 1 and r(CL) < 1) imply that L-lactide monomer added preferentially into the copolymer chain end in the first step of the reaction, resulting in the formation of long blocks of lactidyl unit in the polymer chain. The copolymer composition has a profound influence on the values of L-LL(e) and L-C(e). Both L-LL(e) and L-C(e) increased as the relative proportions of their respective monomers increased. The transesterification coefficient of the second mode of lactidyl units (T-II [CLC]) increased as the feed mole fraction of epsilon-CL increased. In terms of the overall feed compositions, the L-LL(r) values calculated from the reactivity ratio exceeded the L-LL(e) values determined from the product; however, the L-C(r) values were identical or shorter than the L-C(e) values. Therefore, the repeat unit sequence distribution of the copolymers was varied more or less toward a random sequence distribution by variation in the comonomer feed ratio and reaction time. The thermal properties and crystallization of the copolymers were investigated by DSC and XRD. The results showed that a close relationship between copolymer crystallinity and the length of the copolymer sequences. All copolymers of L-LA and epsilon-CL exhibited a single T-gs determined from the second heating scan. The experimental T-gs were in agreement with the calculated T-gs values from Fox equation. It can be concluded that the copolymers are random, or comprise a mixture of compatible block copolymers.

Block Copolymerization of ϵ‐Caprolactone and L‐Lactide by Lanthanum tris(2,6‐Dimethylphenolate)s

Block Copolymerization of ε-Caprolactone and L-Lactide by Lanthanum tris(2,6-Dimethylphenolate)s

Synthesis of Cyclic and Linear Block Copolyesters via Ring-opening Copolymerization of epsilon-Caprolatone and L-Lactide Catalyzed by Zinc Complex

Ring-opening Copolymerization of Ε -Caprolactone and Δ -Valerolactone Catalyzed by a 2,6-Bis(amino)phenol Zinc Complex

Ring-opening Copolymerization of L-Lactide and delta-Valerolactone Catalyzed by Benzoxazolyl Urea Catalyst/MTBD

l-Lactide homopolymerization and l-lactide-ε-caprolactone block copolymerization by lanthanide tris(2,4,6-trimethylphenolate)s

Controlled Synthesis of L -Lactide- B -Ε-caprolactone Block Copolymers Using a Rare Earth Complex As Catalyst

Lanthanum Heterocyclic Schiff-base Complex Initiated Ring-Opening Polymerization of Ɛ-Caprolactone

Ring‐opening Polymerization of Ε‐caprolactone by Lanthanide Tris (2, 6‐dimethylphenolate) S

STUDIES ON COPOLYMERIZATION OF L-LACTIDE WITH Ε-Caprolatone CATALYZED BY MAGNESIUM OCTOATE AND THE STRUCTURE AND PROPERTIES OF THE COPOLYMERS

L-lactide Homopolymerization and Copolymerization with Ɛ-Caprolactone by Tetrahydrosalen Stabilized Yttrium Borohydride Complex

Characteristics, Kinetics And Mechanism Of Epsilon-Caprolactone Polymerization By Lanthanide Tris(2.6-Dimethylphenolate)S

Characteristics, Linetics and Mechanism of ε-Caprolactone Polymerization by Lanthanide Tris(2.6-dimethylphenolate)s

Synthesis Of Poly(Epsilon-Caprolactone)-Poly(L-Lactide) Block Copolymers By Melt Or Solution Sequential Copolymerization Using Nontoxic Dibutylmagnesium As Initiator

Microstructure analysis and thermal properties of l-lactide/ɛ-caprolactone copolymers obtained with magnesium octoate

Triblock and pentablock copolymerizations of ε-caprolactone with L-lactide catalyzed by N-heterocyclic carbene

Selective Transesterification to Control Copolymer Microstructure in the Ring-Opening Copolymerization of Lactide and ε-Caprolactone by Lanthanum Complexes

Ring-opening Polymerization of Cyclic Esters Mediated by Zinc Complexes Coordinated with Benzotriazo-Based Imino-Phenoxy Ligands

Homo-and Copolymerization of Ε-Caprolactone and 2,2-Dimethyltrimethylene Carbonate by Rare Earth Initiators

Polymerization characteristics of epsilon-caprolactone at low temperature by lanthanum tris(2,6-di-tert-butyl-4-methylphenolate) and the block copolymerization of epsilon-caprolactone with cyclic carbonates

Bipyridine-phenolate Based Aluminum Complexes Mediated Ring-Opening Polymerization of Ε-Caprolactone and Lactides with a High Stereoselectivity