Abstract:Using sodium fluoride and rare earth nitrate as raw materials and sodium citrate as surfactant, micron grade NaYF4 upconversion luminescent materials were prepared by hydrothermal method. By X-ray diffraction(XRD), scanning electron microscope(SEM) and fluorescence spectrometer, the crystal phase, morphology and luminescent characteristics of the prepared samples were investigated. The results showed that the phase of the samples could generate a transition from cubic phase to hexagonal phase by adjusting the proportion (5, 6, 7, 8, 9, 11) of NaF/RE , and the X ray diffraction peaks for the cubic and hexagonal phase of samples exactly matched with those of the standard card of PDF# 77-2042 and PDF# 16-0334, respectively. The SEM photographs showed that the crystallinity of samples was high and the dispersibility was favourable, the morphology were translated from microrods to hexagonal microplates. The samples upconversion luminescent spectra showed the intensity enhancement of red and green light emission peaks with increasement of the ratio of NaF/RE3+. The green emission peaks of samples at 520 and 539 nm corresponded to the ²H¹¹/²-⁴-->I₁₅/₂ and ⁴S₃/₂-->⁴I₁₅/₂ level transition of Er³⁺ ion, and the red light emission peaks of samples at 653 nm corresponded to the ⁴F₉/₂-->⁴I₁₅/₂ levelt ransition of Er+ ion. The chromaticity coordinate diagram exhibited that the change of the luminescent color of samples could be achieved by adjusting the ratio of NaF/RE³⁺. With the increasing of NaF/RE³⁺ ratio, for the whole light-emitting colors of samples, the shift from yellow region to near red region could be realized. It can be concluded that through the relatively simple experimental procedure and lower cost materials, the change of phase and morphology, the moving of light-emitting color for sample NaYF4:Yb³⁺, Er³⁺ could be well controlled only by changing the single component (NaF) molar ratio in the raw materials. The effect of phase and morphology of fluorescent materials on their upconversion luminescence has great potential applications in photonic devices and bioanalysis research.

Phase-, Shape- and Size-Controlled Synthesis of NaYF4:Yb3+,Er3+ Nanoparticles Using Rare-Earth Acetate Precursors

Hydrothermal Synthesis and Upconversion Luminescence of Yb3+/Er3+ Co-doped BaY2F8 Nanoparticles

Size- and Phase-Controlled Synthesis of Monodisperse NaYF4:Yb,Er Nanocrystals from a Unique Delayed Nucleation Pathway Monitored with Upconversion Spectroscopy

A Simple Strategy for the Controlled Synthesis of Ultrasmall Hexagonal-Phase NaYF4:Yb,Er Upconversion Nanocrystals

Crystalline Phase and Morphology Controlling to Enhance the Up-Conversion Emission from NaYF4:Yb,Er Nanocrystals

Hexadecylpyridinium Chloride Mediated Hydrothermal Synthesis of NaYF₄:Yb, Er Nanocrystal and Their Luminescent Properties

Lattice Strain Enhanced Phase Transformation of NaYbF4: 2% Er3+ Upconverting Nanoparticles by Tuning the Molar Ratio of Na+/Yb3+

Controlled Synthesis of Monodisperse Hexagonal NaYF₄:Yb/Er Nanocrystals with Ultrasmall Size and Enhanced Upconversion Luminescence

Oleylamine-Mediated Synthesis Of Small Naybf4 Nanoparticles With Tunable Size

Synthesis, characterization, and biological application of size-controlled nanocrystalline NaYF4:Yb,Er infrared-to-visible up-conversion phosphors

Hydrothermal Synthesis and Upconversion Properties of α-NaYF4:Yb3+, Er3+ Nanocrystals Using Citric Acid as Chelating Ligand and NaNO3 as Mineralizer

Synthesis of small-sized hexagonal NaREF4 (RE = Yb, Lu) nanocrystals through accelerating phase transformation

Shape, size, and phase-controlled rare-Earth fluoride nanocrystals with optical up-conversion properties.

Controllable hydrothermal synthesis of NaYbF4 and YbF3 with diverse morphologies and emission enhancement in β-NaYbF4: Er3+ upconversion micro-crystals via solvents codoping and Na+ dosage

Synthesis of NaYF4 Nanocrystals with Predictable Phase and Shape

Hexagonal Phase Beta-Nayf4:Yb/Er Films Made By Electrodepositing Onto Beta-Nagdf4 Underlayer At Low Temperature

Synthesis of Complex Rare Earth Fluoride Nanocrystal Phosphors

Synthesis and Characterization of NaYF4 :Eu Monodisperse Rare-Earth Nanocrystal

Controlled synthesis and characterization of NaYF4:Yb/Er upconverting nanoparticles produced by laser ablation in liquid

Morphology and Phase Selective Synthesis of EuF3 Nanostructures by Polyelectrolyte Assisted Chemical Reaction and Their Optical Properties

[The Different Phase, Morphology Controllable Synthesis and Luminescent Properties Investigation of NaYF⁴: Yb, Er]