Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Facile Synthesis of 3d Porous Flower-Like Zno Micro/Nanostructure Films and Their Photocatalytic Performance

Facile Fabrication of Porous ZnO by a Template Free Method

Nanostructured Porous Zno Film with Enhanced Photocatalytic Activity

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Growth of 3-D Flower/Grass-Like Metal Oxide Nanoarchitectures Based on Catalyst-Assisted Oxidation Method

Porous zinc oxide films: Controlled synthesis, cytotoxicity and photocatalytic activity

Enhanced Photocurrent and Photocatalytic Properties of Porous ZnO Thin Film by Ag Nanoparticles

Facile Preparation of Porous Flower-Like ZnO Microspheres with Excellent Photocatalytic Performance

A Facile Synthesis of Novel ZnO Structures and Their Applications in Photocatalysis

A Novel Synthesis and Excellent Photodegradation of Flower-Like Zno Hierarchical Microspheres

Morphology-controlled Synthesis of Flowerlike ZnO Nano/microstructures and Their Photocatalytic Property.

Synthesis of Snowflake-Like Multi-Layered Zno with Controllable Pore Sizes and Its Photocatalytic Property

Low-temperature Hydrothermal Synthesis of Flower-Like ZnO Microstructure and Nanorod Array on Nanoporous TiO2 Film

Exploiting Electrodeposited Flower-Like Zn4(OH)6SO4·4H2O Nanosheets As Precursor for Porous ZnO Nanosheets

Synthesis of ZnO Nanoflowers and Their Wettabilities and Photocatalytic Properties.

Shape-controlled fabrication of porous ZnO architectures and their photocatalytic properties

Facile Synthesis of Ag/ZnO Micro-Flowers and Their Improved Ultraviolet and Visible Light Photocatalytic Activity

Zn3V2O7(OH)2(H2O)2 and Zn3V2O8 Nanostructures: Controlled Fabrication and Photocatalytic Performance

Evolution of ZnO Architecture on a Nanoporous TiO2film by a Hydrothermal Method and the Photoelectrochemical Performance

Hierarchical Zno Microarchitectures Assembled by Ultrathin Nanosheets: Hydrothermal Synthesis and Enhanced Photocatalytic Activity

Morphology-controlled synthesis of ZnO 3D hierarchical structures and their photocatalytic performance