Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Shape-controlled fabrication of porous ZnO architectures and their photocatalytic properties

Facile Fabrication of Porous ZnO by a Template Free Method

Shape-controlled Synthesis of Bare ZnO Nanomaterials with Improved Photoactivity and Photostability

Structural and Optical Properties of Porous ZnO Nanorods Synthesized by a Simple Two-Step Method

Large Scale Synthesis of Porous ZnO Hollow Structures with Tunable Diameters and Shell Thicknesses

Controllable Zno Architectures Synthesised on Zinc Substrates by Hydrothermal Preparation for Enhanced Photocatalytic Activity

Fabrication of ZnO with tunable morphology through a facile treatment of Zn-based coordination polymers

Porous zinc oxide films: Controlled synthesis, cytotoxicity and photocatalytic activity

Orientable Pore-Size-distribution of ZnO Nanostructures and Their Superior Photocatalytic Activity

Controllable Preferential-Etching Synthesis and Photocatalytic Activity of Porous ZnO Nanotubes

Porous ZnO Sheets Transformed from Zinc Sulfate Hydroxide Hydrate and Their Photoluminescence Performance

Controllable Synthesis of ZnO Hierarchical Architectures and Their Photocatalytic Property

Morphology-controllable electrochemical synthesis and photoluminescence properties of ZnO nanocrystals with porous structures

Synthesis of Snowflake-Like Multi-Layered Zno with Controllable Pore Sizes and Its Photocatalytic Property

Controlling Morphologies and Tuning the Related Properties of Nano/Microstructured ZnO Crystallites

Shape-controlled zinc(II) oxide nanomaterial constructed from three-dimensional zinc(II) coordination complex

Controllable Preparation and Photocatalytic Activity of ZnO Microstructures with Different Morphology

Hierarchically Assembled Porous ZnO Nanoparticles: Synthesis, Surface Energy, and Photocatalytic Activity

Controlled Fabrication of Nanostructured ZnO Particles and Porous Thin Films Via a Modified Chemical Bath Deposition Method

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Complex and oriented ZnO nanostructures