Abstract:This study aimed to investigate the impact resistance of monolithic and laminated polycarbonate plates for windshields in motorsport applications through a coupled experimental-numerical study. Both low- and high-velocity impact tests were performed by using a drop tower and a gas gun, respectively, considering a sharp-edged projectile impacting on flat panels. The response of the polycarbonate plates was evaluated in terms of the failure mode, perforation velocity threshold, and energy absorption mechanism. The experiments allowed for the assessment and the generalization of a 3D finite element modeling approach originally developed for supersonic application based on different state-of-the-art constitutive theories, including temperature-dependent and rate-dependent von Mises plasticity coupled with ductile damage, Mie-Grüneisen equation of state, and temperature variation due to energy dissipation under adiabatic assumptions. The approach was completed with a cohesive zone model for a laminate plate and studies were performed to highlight the relevancy of different aspects of material characterization. The tests and numerical analyses performed at different velocity ranges highlight the importance of viscoplastic behavior in a polycarbonate windshield. The numerical approach showed its capability to model the different failure modes for monolithic and laminated panels and capture the perforation velocity thresholds with appreciable accuracy, which were actually found to be quite similar for the two types of panels in the test conditions considered. A numerical investigation suggests that the development of delaminations could lead to the improved energy absorption of laminated polycarbonate. To further assess the numerical model, it was used to successfully predict the penetration threshold velocity of a polycarbonate windshield subjected to a gas gun impact test.

Energy Absorption Mechanism of Polyvinyl Butyral Laminated Windshield Subjected to Head Impact: Experiment and Numerical Simulations

Investigation on Energy Absorption Characteristics of PVB Laminated Windshield Subject to Human Head Impact

Research on Dynamic Response of PVB Laminated Windshield Subjected to Low Velocity Impact

Numerical Study of Pvb Laminated Windshield Cracking Upon Human Head Impact

Review of Research on Impact Response of Automotive Polyvinyl Butyral Laminated Windshield

Head protection characteristics of windshield during pedestrian-vehicle accident

Systematic Experimental Study on Mechanical Behavior of Pvb (polyvinyl Butyral) Material under Various Loading Conditions

Experimental investigation on constitutive behavior of PVB under impact loading

Deformation and Damage Mechanisms of Laminated Glass Windows Subjected to High Velocity Soft Impact

Study of damage in windshield glazing subject to impact by a pedestrian's head

Experimental study on mechanical behavior of PVB laminated glass under quasi-static and dynamic loadings

Experimental Study of Headform–pvb Laminated Windshield Impact

Soft Impact Response of Laminated Glass Plates

Crack Analysis in PVB Laminated Windshield Impacted by Pedestrian Head in Traffic Accident

Influencing Factors Analysis in Simulation of Head-Windscreen Laminated Glass Impacting

Impact Fracture Simulation of Laminated Glass Based on Thick Shell Elements and a Cohesive Zone Model

Investigation on Behavior of Glazing System with Elastomeric Interlayers under Blast Effects

Modeling And Experimental Studies Of Crack Propagation In Laminated Glass Sheets

Research on Temperature and Strain Rate Dependent Viscoelastic Response of Polyvinyl Butaral Film

Impact Response of Monolithic and Laminated Polycarbonate Panels: An Experimental and Numerical Investigation

Study For Windshield Against Bird-Impact By Simulation And Experiment