Abstract:To separate Mo(VI) and Zr(IV) ions from a 0.5 M oxalic acid solution and from each other, a novel macroporous silica-based N,N,N′,N′- tetraoctyl-3-oxapentane-1,5-diamide (TODGA) chelating polymeric adsorbent (TODGA/SiO 2 -P) was synthesized by introducing the TODGA molecule into ca. 50-μm diameter SiO 2 -P particles by impregnation. The adsorption of Mo(VI) and Zr(IV) ions onto TODGA/SiO 2 -P was investigated by examining the influence of nitric acid and oxalic acid concentrations. It was found that the adsorption was strongly affected by increasing the HNO 3 concentration from 0.5 M to 9.0 M either with or without the addition of 0.5 M H 2 C 2 O 4 . In the absence of 0.5 M H 2 C 2 O 4 , the distribution coefficients (K d ) of both Mo(VI) and Zr(IV) ions decreased with an increase in the HNO 3 concentration from 0.5 M to 3.0 M, increased slowly when the concentration of HNO 3 was increased further from 3.0 M to 6.0 M, and then increased gradually above 6.0 M concentration. Furthermore, the adsorption of Zn(IV) ions onto TODGA/SiO 2 -P was considerably greater than that of Mo(VI) ions. In the presence of 0.5 M H 2 C 2 O 4 , Zr(IV) ions showed no adsorption at HNO 3 concentrations below 4.0 M, being partly adsorbed in the presence of 4.0–6.0 M HNO 3 and fully adsorbed when the HNO 3 concentration was greater than 6.0 M. In contrast, Mo(VI) ions showed a much lower adsorption at HNO 3 concentrations below 2.0 M and no adsorption above this acid level. In the presence of HNO 3 at a concentration above 6.0 M and containing 0.5 M H 2 C 2 O 4 , the adsorption of Zr(IV) ions overlapped that from a similar HNO 3 solution which did not include 0.5 M H 2 C 2 O 4 . This was attributed to complete protonation of the C 2 O 2− 2 anion. On the basis of batch experiments, Mo(VI) and Zr(IV) ions were separated from a 6.5 M HNO 3 solution containing 0.5 M H 2 C 2 O 4 by means of a column packed with TODGA/SiO 2 -P at 50°C. The separate components, Mo(VI) and Zr(IV), could be effectively separated from each other by eluting with some selected eluants. The recovery percentage was 100.5% for Mo(VI) ions and 96.8% for Zr(IV) ions.

Adsorption Characteristics of Trivalent Rare Earths and Chemical Stability of a Silica-Based Macroporous TODGA Adsorbent in HNO3Solution

Impregnation synthesis of a novel macroporous silica-based TODGA polymeric composite and its application in the adsorption of rare earths in nitric acid solution containing diethylenetriaminepentaacetic acid

Preparation of A Novel Macroporous Silica-Based Diglycolamide Derivative-Impregnated Polymeric Composite and Its Adsorption Mechanism for Rare Earth Metal Ions

Synthesis of Two Novel Macroporous Silica-Based Impregnated Polymeric Composites and Their Application in Highly Active Liquid Waste Partitioning by Extraction Chromatography

Synthesis of a Novel Silica‐Based Macroporous Polymer Containing TODGA Chelating Agent and Its Application in the Chromatographic Separation of Mo(VI) and Zr(IV) from Diethylenetriaminepentaacetic Acid

Group Partitioning of Minor Actinides and Rare Earths from Highly Active Liquid Waste by Extraction Chromatography Utilizing Two Macroporous Silica-Based Impregnated Polymeric Composites

Preparation of a Novel Macroporous Silica-Based 2,6-Bis(5,6-diisobutyl-1,2,4-triazine-3-yl)pyridine Impregnated Polymeric Composite and Its Application in the Adsorption for Trivalent Rare Earths

Chromatographic Separation of Strontium (II) from a Nitric Acid Solution Containing Some Typically Simulated Elements by a Novel Silica‐Based TODGA Impregnated Polymeric Composite in the MAREC Process

Efficient Separation of Th(IV) from Highly Acidic Solution by Microporous Resin Materials Containing Two Novel Phenanthroline Phosphonates

Separation of Minor Actinides and Rare Earths from a Simulated High Activity Liquid Waste by Two Macroporous Silica‐based Polymeric Composites

Adsorption of Some Typical Fission Products onto a Novel Macroporous Silica-based Dialkyl Derivative of Pyridine Impregnated Material

SPEC Process II. Adsorption of Strontium and Some Typical Co-Existent Elements Contained in High Level Liquid Waste Onto a Macroporous Silica-Based Crown Ether Impregnated Functional Composite

Adsorption Behavior of Sr(II) and Some Typical Co‐existent Metals Contained in High Level Liquid Waste Onto a Modified Macroporous Silica‐Based Polymeric DtBuCH18C6 Composite

Synthesis and Application of A Macroporous Silica-Based Polymeric Octyl(Phenyl)-N,N-Diisobutylcarbamoylmethylphoshine Oxide Composite for the Chromatographic Separation of High Level Liquid Waste

Application of a Macroporous Silica-Based CMPO-Impregnated Polymeric Composite in Group Partitioning of Long-Lived Minor Actinides from Highly Active Liquid by Extraction Chromatography

Bleeding evaluation of the stationary phase from a few novel macroporous silica-substrate polymeric materials used for radionuclide partitioning from HLLW in MAREC process

Removal of Pd(II), Zr(IV), Sr(II), Fe(III), and Mo(VI) from simulated high level liquid waste by extraction chromatography utilizing the macroporous silica-based polymeric materials

Adsorption and Chromatographic Separation of Mo(VI) and Zr(IV) Ions from a High-Concentration Oxalic Acid Solution by a Macroporous Silica-Based N,N,N′,N′-Tetraoctyl-3-Oxapentane-1,5-Diamide Polymeric Adsorbent

Adsorption of Cesium and Some Typical Coexistent Elements Onto a Modified Macroporous Silica-Based Supramolecular Recognition Material.

Properties and Mechanism of Molybdenum and Zirconium Adsorption by a Macroporous Silica‐Based Extraction Resin in the MAREC Process

Improvement in the elution performance of an N,N,N',N-tetraoctyl diglycolamide impregnated extraction chromatography adsorbent using neodymium via micro-particle-induced X-ray emission analysis