Abstract:To separate Mo(VI) and Zr(IV) ions from a 0.5 M oxalic acid solution and from each other, a novel macroporous silica-based N,N,N′,N′- tetraoctyl-3-oxapentane-1,5-diamide (TODGA) chelating polymeric adsorbent (TODGA/SiO 2 -P) was synthesized by introducing the TODGA molecule into ca. 50-μm diameter SiO 2 -P particles by impregnation. The adsorption of Mo(VI) and Zr(IV) ions onto TODGA/SiO 2 -P was investigated by examining the influence of nitric acid and oxalic acid concentrations. It was found that the adsorption was strongly affected by increasing the HNO 3 concentration from 0.5 M to 9.0 M either with or without the addition of 0.5 M H 2 C 2 O 4 . In the absence of 0.5 M H 2 C 2 O 4 , the distribution coefficients (K d ) of both Mo(VI) and Zr(IV) ions decreased with an increase in the HNO 3 concentration from 0.5 M to 3.0 M, increased slowly when the concentration of HNO 3 was increased further from 3.0 M to 6.0 M, and then increased gradually above 6.0 M concentration. Furthermore, the adsorption of Zn(IV) ions onto TODGA/SiO 2 -P was considerably greater than that of Mo(VI) ions. In the presence of 0.5 M H 2 C 2 O 4 , Zr(IV) ions showed no adsorption at HNO 3 concentrations below 4.0 M, being partly adsorbed in the presence of 4.0–6.0 M HNO 3 and fully adsorbed when the HNO 3 concentration was greater than 6.0 M. In contrast, Mo(VI) ions showed a much lower adsorption at HNO 3 concentrations below 2.0 M and no adsorption above this acid level. In the presence of HNO 3 at a concentration above 6.0 M and containing 0.5 M H 2 C 2 O 4 , the adsorption of Zr(IV) ions overlapped that from a similar HNO 3 solution which did not include 0.5 M H 2 C 2 O 4 . This was attributed to complete protonation of the C 2 O 2− 2 anion. On the basis of batch experiments, Mo(VI) and Zr(IV) ions were separated from a 6.5 M HNO 3 solution containing 0.5 M H 2 C 2 O 4 by means of a column packed with TODGA/SiO 2 -P at 50°C. The separate components, Mo(VI) and Zr(IV), could be effectively separated from each other by eluting with some selected eluants. The recovery percentage was 100.5% for Mo(VI) ions and 96.8% for Zr(IV) ions.

Synthesis of a Novel Silica‐Based Macroporous Polymer Containing TODGA Chelating Agent and Its Application in the Chromatographic Separation of Mo(VI) and Zr(IV) from Diethylenetriaminepentaacetic Acid

Adsorption and Chromatographic Separation of Mo(VI) and Zr(IV) Ions from a High-Concentration Oxalic Acid Solution by a Macroporous Silica-Based N,N,N′,N′-Tetraoctyl-3-Oxapentane-1,5-Diamide Polymeric Adsorbent

Properties and Mechanism of Molybdenum and Zirconium Adsorption by a Macroporous Silica‐Based Extraction Resin in the MAREC Process

Impregnation synthesis of a novel macroporous silica-based TODGA polymeric composite and its application in the adsorption of rare earths in nitric acid solution containing diethylenetriaminepentaacetic acid

Chromatographic Separation of Strontium (II) from a Nitric Acid Solution Containing Some Typically Simulated Elements by a Novel Silica‐Based TODGA Impregnated Polymeric Composite in the MAREC Process

Preparation of A Novel Macroporous Silica-Based Diglycolamide Derivative-Impregnated Polymeric Composite and Its Adsorption Mechanism for Rare Earth Metal Ions

Synthesis of Two Novel Macroporous Silica-Based Impregnated Polymeric Composites and Their Application in Highly Active Liquid Waste Partitioning by Extraction Chromatography

Removal of Pd(II), Zr(IV), Sr(II), Fe(III), and Mo(VI) from simulated high level liquid waste by extraction chromatography utilizing the macroporous silica-based polymeric materials

Synthesis and Application of A Macroporous Silica-Based Polymeric Octyl(Phenyl)-N,N-Diisobutylcarbamoylmethylphoshine Oxide Composite for the Chromatographic Separation of High Level Liquid Waste

SPEC Process III. Synthesis of a Macroporous Silica-based Crown Ether-impregnated Polymeric Composite Modified with 1-Octanol and its Adsorption Capacity for Sr(II) Ions and Some Typical Co-existent Metal Ions

Preparation of A Novel Silica-Based Dtbuch18c6 Impregnated Polymeric Composite Modified by Tri-N-Butyl Phosphate and Its Application in Chromatographic Partitioning of Strontium from High Level Liquid Waste

Adsorption of Some Typical Fission Products onto a Novel Macroporous Silica-based Dialkyl Derivative of Pyridine Impregnated Material

Bleeding evaluation of the stationary phase from a few novel macroporous silica-substrate polymeric materials used for radionuclide partitioning from HLLW in MAREC process

Preparation of A Macroporous Silica-Based Multidentate Soft-Ligand Material and Its Application in the Adsorption of Palladium and the Others

Impregnation synthesis of a novel macroporous silica-based crown ether polymeric material modified by 1-dodecanol and its adsorption for strontium and some coexistent metals

Synthesis of a Macroporous Silica‐based Derivative of Pyridine Material and Its Application in Separation of Palladium

Preparation of a Novel Macroporous Silica-Based 2,6-Bis(5,6-diisobutyl-1,2,4-triazine-3-yl)pyridine Impregnated Polymeric Composite and Its Application in the Adsorption for Trivalent Rare Earths

Molecular Modification of a Novel Macroporous Silica-Based Impregnated Polymeric Composite by Tri-N-butyl Phosphate and Its Application in the Adsorption for Some Metals Contained in a Typical Simulated HLLW.

Minor Actinides Partitioning: Uptake of Palladium with Triazine-Containing Adsorbent under the Framework of Spmp Process

Separation of Minor Actinides and Rare Earths from a Simulated High Activity Liquid Waste by Two Macroporous Silica‐based Polymeric Composites

Modification Of A Novel Macroporous Silica-Based Crown Ether Impregnated Polymeric Composite With 1-Dodecanol And Its Adsorption For Some Fission And Non-Fission Products Contained In High Level Liquid Waste