Austenite Grain Growth Kinetics in Continuously Cast Low Alloyed Steels at High Temperature
Peng Lan,Huasong Liu,Lirui Zhang,Yifan Lu,Jiaquan Zhang,Liang Chen,Rongyu Wen,Pu Wang
DOI: https://doi.org/10.1007/s11663-024-03347-0
2024-01-01
Metallurgical and Materials Transactions B
Abstract:The austenite grain growth behavior at high temperature of 1300 °C 1450 °C for different peritectic steels was investigated by isothermal experiment and kinetic modeling. It is found that the grain growth behavior is quite distinct for different low alloyed steels even if the carbon equivalent is close. The grain size in the steel with only 0.4 pct Mn alloying is about 1300 μm after soaking for 900 seconds at 1400 °C, while that is just about 200 μm for the 0.9 pct Mn + 1.2 pct Cr alloyed steel. Such a big difference is the result of solute drag effect according to thermodynamic calculation. The kinetic model for austenite grain growth at high temperature was mathematically developed, and the parameters determined by linear regression for different steels are quite distinct. The time exponent and activation energy in the model are piecewise fitting at different temperature range. For the common low alloyed steels, ideal grain growth at 1400 °C 1450 °C is depicted by time exponent of 0.5. However, for Ti-added steel and Cr alloyed steels, the time exponent is just between 0.25 and 0.35 for the whole temperature range. The grain boundary mobility in different steels at various temperatures is also quite different. The intrinsic grain boundary migration can only be achieved when the time exponent is equal to 0.5 for common low alloyed steel. For Ti-added steel and Cr alloyed steel with small grain boundary mobility restricted by particle pinning or solute drag, it is much lower than 0.5. High grain boundary mobility leads to an overestimation on austenite grain growth, especially for steel with high solute content at low temperature. By comparing the results from references, it is confirmed that the present model is capable to describe the austenite grain growth at lower cooling rate than 0.5 °C/s, corresponding to the subsurface or internal matrix during continuous casting. It is incompetent for the surface layer where cooling rate is higher than 5 °C/s, as the predicted grain size is much smaller than the measured. Considering the grain growth behavior at elevated temperature in the experiment, the austenite grain coarsening should mainly occur in the mold with a grain boundary mobility much higher than intrinsic level, probably from the attribution of massive transformation.