Transformation character of ferrite formation by a ledge mechanism under a mixed-control model

Zhen-qing Liu,Zhi-gang Yang,Zhao-dong Li,Chi Zhang

DOI: https://doi.org/10.1007/s12613-012-0574-6

2012-01-01

Abstract:A mixed-control model was developed to study the transformation character of ferrite formation by a ledge mechanism. A numerical two-dimensional diffusion-field model was combined to describe the evolution of the diffusion field ahead of the migrating austenite/ ferrite interface. The calculation results show that the bulk diffusion-controlled model leads to a deviation from experimental results under large solute supersaturation. In the mixed-control model, solute supersaturation and a parameter Z together determine the transformation character, which is quantified by the normalized concentration of carbon in austenite at the austenite/ferrite interface. By comparing with experimental data, the pre-exponential factor of interface mobility, M 0, is estimated within the range from 0.10 to 0.60 mol·m·J−1·s−1 for the alloys with 0.11wt%–0.49wt% C at 700–740°C. For a certain Fe-C alloy, the trend of the transformation character relies on the magnitude of M 0 as the transformation temperature decreases.