Abstract:Cu-Ni-Sn alloys are well known for their excellent properties, including excellent elasticity and high strength, which enable large potentials for applications in microelectronic industry and 3D printing for example. Preparation of the high quality spherical powders should meet the new requirements in these emerging fields. In this work, the mono-sized Cu-13Ni-17Sn (wt%) microspheres with controllable diameters ranging from 84.4 mu m to 212.0 mu m were prepared by pulsated orifice ejection method (POEM). Solidified Cu-Ni-Sn microspheres exhibit good sphericity and remarkably narrowed size distribution. The percentage of microspheres with sphericity of more than 0.9 is high up to 98.6%, and the average sphericity of microspheres is 0.989. The surface of Cu-Ni-Sn microspheres is smooth, and the interior contains no pores and impurities. Furthermore, the cooling rate of Cu-13Ni-17Sn microspheres was estimated in a Newton's cooling model. With decreasing particle diameter, the cooling rate of Cu-13Ni-17Sn microspheres increases gradually. When the particle diameter is less than 84.4 mu m, the cooling rate of microspheres exceeds 3.64 x 10(4) K s(-1). With increasing particle size, the secondary dendrite arm spacing increases gradually owing to the decrease of the sphere cooling rate.

Fabrication of Hollow Nickel Micro-Spheres with High Degree of Hollowness by Silicon Powder-Mixed Spark Erosion

Preparation and solidification process of mono-sized Cu-Ni-Sn microspheres by pulsated orifice ejection method

Fabrication of Nickel hollow spheres by microemulsion–template–interface reaction route

Large Scale Fabrication of NiS Hollow Spheres with Controllable Diameter Sizes

Hollow and solid spherical magnetostrictive particulate composites

Submicrometer-sized hollow nickel spheres synthesized by autocatalytic reduction

Facile synthesis of hollow and porous nickel microspheres by low temperature molecular self-assembly

Preparation and Microwave Characterization of Submicrometer-Sized Hollow Nickel Spheres

A Novel Method for the Fabrication of Monodisperse Hollow Silica Spheres

A Method for the Fabrication of Monodisperse Hollow Silica Spheres

Preparation of micrometer- and nanometer-sized hollow nickel spheres by autocatalytic reduction

Nanometer‐Sized Nickel Hollow Spheres

Facile Fabrication Method And Characterization Of Hollow Ag/Sio2 Double-Shelled Spheres

Fabrication of Hollow (ni0.8co0.1mn0.1) [ozgur, 2010 #912]oy Spheres by Ultrasonic Spray Pyrolysis Method

A New Method for the Preparation of Monoporous Hollow Microspheres

Fabrication of microspherical Hexanitrostilbene (HNS) with droplet microfluidic technology

Use of Carbonaceous Polysaccharide Microspheres As Templates for Fabricating Metal Oxide Hollow Spheres

Facile approach for the fabrication of monodisperse hollow silica spheres

Large-scale Fabrication of Silicon Carbide Hollow Spheres

Study on formation of submicrometer-sized hollow nickel spheres by autocatalytic reduction method

Controlled fabrication of uniform hollow bowl-shaped microspheres based on polyphosphazene material