Abstract:Although the synthesis of novel nanostructured metal sulfides has been well established, further size‐controllable optimization is still valuable to enhance their performance for various applications. Herein, a self‐template method to size‐controllably synthesize the hollow NiCo2S4 nanospheres is reported. Uniformly monodisperse NiCo precursors with diameter widely ranging from 97 to 550 nm are controllably synthesized and subsequently transformed into hollow NiCo2S4 nanospheres through in situ sulfidation. Smaller nanoparticles' diameter results in the hollow NiCo2S4 nanospheres larger surface area and thinner shell thickness and hence provides much more electrochemical active sites as well as facilitate the ion and electron transfer. Consequently, the hollow NiCo2S4 nanospheres—used as the electrode materials in supercapacitors—achieve 19% enhancement of specific capacity from 484.8 to 575.1 C g−1 through lowering the 42.5% diameter of hollow NiCo2S4 nanospheres from 407 to 234 nm. Moreover, the hollow NiCo2S4 nanospheres with 234 nm diameter exhibit superior rate capacity indicated by 49% capacity retention from 1 to 50 A g−1 and excellent cycling stability (77% after 2000 cycles). Furthermore, this method is a potentially general strategy in the size‐controllable synthesis of the metal sulfides hollow nanostructures and results in the remarkable electrochemical applications.

Large Scale Fabrication of NiS Hollow Spheres with Controllable Diameter Sizes

Tailoring Pore Size of Nitrogen‐Doped Hollow Carbon Nanospheres for Confining Sulfur in Lithium–Sulfur Batteries

Preparation Of Nis Hollow Microspheres By Solvothermal Method

Nanometer‐Sized Nickel Hollow Spheres

Sustainable Synthesis of N‐Doped Hollow Porous Carbon Spheres Via a Spray‐Drying Method for Lithium‐Sulfur Storage with Ultralong Cycle Life

Metal oxide and sulfide hollow spheres: layer-by-layer synthesis and their application in lithium-ion battery.

Fabrication of monodisperse CdS hollow spheres

PVP-assisted synthesis of hollow Ni0.75Zn0.25Fe2O4 nanospheres for lithium-ion batteries

Amorphous Ni-P Hollow Spheres Prepared By Self-Assembly Of Ni-P Nanoparticles On Polystyrene Beads

Amorphous Ni-B hollow spheres synthesized by controlled organization of Ni-B nanoparticles over PS beads via surface seeding/electroless plating

Fabrication of 1D nickel sulfide nanocrystals with high capacitances and remarkable durability

Formation of Uniform Flowerlike Patterns of NiS by Macrocycle Polyamine Assisted Solution-Phase Route

Formation of Hollow Submicrometer Spheres of Nickel Selenides

Synthesis of Size‐Controllable NiCo 2 S 4 Hollow Nanospheres Toward Enhanced Electrochemical Performance

Size-engineerable NiS2 hollow spheres photo co-catalysts from supermolecular precursor for H2 production from water splitting

Low Temperature Interface-Mineralizing Route to Hollow CuS, CdS, and NiS Spheres

Synthesizing Ordered Mesoporous Ni Spheres with Uniform and Adjustable Size Through a One-Step Pd2+-assisted Soft-Templating Strategy.

Hydrothermal Preparation and High Electrochemical Performance of NiS Nanospheres as Anode for Lithium-Ion Batteries

Preparation of NiCo2S4/carbon hollow sphere for long cycle lithium sulfur batteries

Facile Synthesis of Fe3S4hollow Spheres with High-Performance for Lithium-Ion Batteries and Water Treatment

Fabrication of polymeric hollow nanospheres, hollow nanocubes and hollow plates