Fatigue Test on U-Rib-to-Deck Connections in Orthotropic Steel Bridge Decks
Xing-han YE,Yi-shan CAO,Xing-er CAO,Bin CHENG
DOI: https://doi.org/10.3969/j.issn.1002-0268.2017.09.010
2017-01-01
Journal of Highway and Transportation Research and Development
Abstract:In order to deeply investigate the fatigue behavior and failure mechanism of U-rib-to-deck weld connections in orthotropic steel bridge decks, 6 full-scale specimen models are fabricated for the experimental study. The static tests, where load cases of centric and eccentric loadings are both conducted, and the stresses on the steel surfaces near welds are recorded to obtain the hot spot stress distributions and the stress concentration factors at first. High-cycle repeated loading are subsequently applied to the specimens with different hot spot stress ranges, and the measured data including failure pattern, fatigue life, crack propagation process, crack growth rate, as well as rigidity degradation of the specimens are obtained. The result shows that (1) the weld toes on deck plate provide the highest hot spot stresses of U-rib-to-deck weld connections;(2) the fatigue crack propagation process of the connections under repeated loading could be divided into 4 stages, i. e. , crack initiation, crack stable propagation, crack running through plate thickness, and fracture failure, and the residual fatigue lives after the crack running through plate thickness could be neglected;(3) the crack growth rates in the initial stage are stable, while the growth rates after running through plate thickness are obviously accelerated;(4) degradations of connection rigidities are first observed for specimens when the single crack has been accumulated to be 150 mm long and could be significantly aggravated when the crack has run through the plate thickness. Conservatively, based on the comparison of fatigue lives, the FAT100 S-N curve as provided in the International Institute Welding ( IIW ) fatigue recommendation could be used to predict the fatigue lives of such U-rib-to-deck welded connections in orthotropic steel bridge decks.