Abstract:Physicochemical, surface, and mechanical properties of three batches of T800 grade carbon fibers (CFs) treated with three kinds of sizing agents and Toray T800H CFs were characterized to study the effect of sizing agents on surface properties. Scanning electron microscopy for morphology, atomic force microscopy calculations, and results for the content of sizing agents showed that sizing agent B improved the surface roughness and CFs with high content of sizing agent always presented small surface roughness in a certain content range 1.2–1.6%. Surface energy of CFs was calculated by Young's contact angle using the test results with water and glycol, and contact angles with LY-1 and modified-AC531 were also acquired. The results proved that CFs of sizing agent group B had the highest average surface energy and the lowest average contact angles with both LY-1 and modified-AC531. From both single-filament and tensile strength test results, the average strength of CFs of sizing agent group B was found to be the lowest, which indicated that sizing agent B had an influence on tensile strength decrease of T800 grade CFs. Comparing the results of interfacial shear strength both in a natural dry state and after hygrothermal treatment, high surface energy was found to be the key element to obtain high interfacial adhesion between T800 grade CFs and bismaleimide, and high surface roughness and low contact angle also played important roles. Among sizing agents A, B, and C, A had an effect on the interfacial shear strength decrease of CFs in the natural dry state, while C had that after hygrothermal treatment.This article has not yet been cited by other publications.

Home-Made Epoxy Emulsion Sizing Agent for Treating Carbon Fibers: Thermal Stability and Mechanical Properties

Enhanced Interfacial, Mechanical, and Anti-Hygrothermal Properties of Carbon Fiber/cyanate Ester Composites with the Catalytic Sizing Agents of Titanium Epoxy

Effect of Emulsifier Content of Sizing Agent on the Surface of Carbon Fibres and Interface of Its Composites

Properties of Carbon Fiber Sized with Poly(Phthalazinone Ether Ketone) Resin

Effect of Molecular Weight of Self-Emulsifying Amphiphilic Epoxy Sizing Emulsions on the Carbon Fibres and Interfacial Properties of Their Composites

Influence of Sizing Emulsifier Content on the Properties of Carbon Fibers and Its Composites

Effects of Surface Treatment of Carbon Fiber: Tensile Property, Surface Characteristics, and Bonding to Epoxy

Effect of Sizing Agent on the Mechanical, Thermal, and Electrical Performance of Basalt Fiber/Epoxy Composites

Thermal Characterization of Carbon‐nanofiber‐reinforced Tetraglycidyl‐4,4′‐diaminodiphenylmethane/4,4′‐diaminodiphenylsulfone Epoxy Composites

Effect of sizing on the interfacial shear strength of carbon fiber/epoxy resin monofilament composite

Improvement in interfacial shear strength and fracture toughness for carbon fiber reinforced epoxy composite by fiber sizing

Interfacial improvement of carbon fiber reinforced epoxy composites by tuning the content of curing agent in sizing agent

Effect of sizing agents on tensile properties of carbon fiber filament wound structures

Effect of Sizing Agents on Surface Properties of Carbon Fibers and Interfacial Adhesion of Carbon Fiber/Bismaleimide Composites

The Effect of Sizing Agent of Carbon Fibre on the Interface of Electron Beam Cured Composites

Influence of Sizing Molecular Weight on the Properties of Carbon Fibers and Its Composites

Molecular Dynamics Simulations of the Effect of Sizing Agent on the Interface Property in Carbon Fiber Reinforced Vinyl Ester Resin Composite

Mechanism Identification and Kinetics Analysis of Thermal Degradation for Carbon Fiber/Epoxy Resin

Thermal stability of epoxy-silica hybrid materials by thermogravimetric analysis

Preparationof Self‐emulsifying Waterborne Polyamide‐imide Sizing for Carbon Fiber and Improvement on Mechanical Performances of Carbon Fiber Reinforced Thermoplastic Polymer

Study of Heat Treatment Effect on Mechanical Properties of Epoxy Resin Reinforced with Fiber Glass