Optimizing the White Light Emission of Pr3+ Activated SrCeO3 Perovskite by Controlling the Excitation Wavelength for High CRI wLED Applications
C. K. Shilpa,M. V. Abin Prasanth,S. V. Jasira,V. P. Veena,K. M. Nissamudeen
DOI: https://doi.org/10.1007/s10895-024-03651-7
2024-03-14
Journal of Fluorescence
Abstract:The current research illustrates excitation energy-triggered photoluminescent characteristics of Pr 3+ ions in SrCeO 3 providing a practical approach for developing high CRI wLED and its applications. SrCeO 3 : xPr 3+ (x = 0, 0.005, 0.01, 0.02, 0.03 wt) perovskites synthesized by fuel excess gel combustion method generate high CRI (~98) for wLED applications. Crystalline phosphors with orthorhombic structures having space group Pnma were confirmed by XRD. The unit cell volume expansion occurred with an increase in Pr 3+ concentration was verified through the Rietveld refinement technique. Surface morphology, particle distribution, and size were observed via FE-SEM imaging, and detected a well-defined regular distorted spherical structure with average grain size 0.826 μm for Pr 3+ doped SrCeO 3 . Elemental mapping and EDS analysis identified the uniform distribution and elemental purity of SrCeO 3 : 0.01 Pr 3+ . Further, the molecular vibrations and modes were analyzed from the Raman spectrum. Moreover, the average particle size assessed via TEM analysis was found to be ~83.2 nm, consistent with XRD analysis. UV–visible absorption spectra for optical energy-band gap analysis showed a decrease in band gap energy with an increase in Pr 3+ concentration, realizing an effective energy transfer from Ce 4+ to Pr 3+ . PL measurements showed a huge variety of emission transitions, corresponding to excitations 290 nm, 321 nm, 373 nm, and 449 nm. The critical dopant concentration instigated by concentration quenching was 1 wt% Pr 3+ , ascribed to dipole–dipole interaction. The fluorescence lifetime of the optimal sample was 4.835 μs. Commission International de I'Eclairage (CIE) diagram exposes the white light emanation of SrCeO 3 : Pr 3+ . Among which white light with high CRI (~98) and comparably low CCT (~6311 K) was obtained for SrCeO 3 : 0.01 Pr 3+ at 373 nm excitation. The obtained results recommend that SrCeO 3 : Pr 3+ perovskite as an efficient white phosphor for fabricating high-performance wLEDs.
chemistry, physical, analytical,biochemical research methods