Abstract:The inclusion plays a crucial role in mastering mechanical responses and cracking behaviors of brittle materials. In this work, a series of uniaxial compression tests were performed to investigate the effect of infilling composition (i.e., proportion and grain size) on the mechanical responses of brittle materials. Digital image correlation (DIC) and acoustic emission (AE) techniques were applied, respectively, to measure the surface strain and internal AE signals of brittle materials for further analysis of failure behaviors. The results demonstrate that both infilling proportion and grain size significantly influence the cracking processes and failure modes of brittle materials. The uniaxial compressive strength (UCS) and deformation modulus increase with the increase of the cement proportion or infilling grain size due to the stress redistribution around the inclusions. The debonding behavior between inclusion and matrix becomes significant when the specimens have a higher cement proportion or larger grain sizes. Interestingly, the number of accumulative and peak AE events is negatively correlated to the cement proportion and grain size. Three failure modes (tensile failure, shear failure, and mixed failure) are observed, and the mixed failure mode is the dominant one. Using a bonded-particle model (BPM), the numerical results can verify the experimental observation regarding debonding and cracking behaviors based on the full-field stresses and fragment characteristics analysis, and further reveal the failure mechanism of the specimen with infilling with different infilling compositions. Based on elasticity and complex variable theory, the derived dimensionless stresses around the inclusion interface can well explain the debonding behavior with rigid and soft inclusions, which is in reasonable agreement with numerical results. The current study could provide technical grantees for the safety and reliability of practical engineerings such as slope engineering, back-filling in mining, and tunnelling engineering.

Elastic-Plastic Fracture Behavior Analysis On A Griffith Crack In The Cylindrical Three-Phase Composites With Generalized Irwin Model

Mechanical behavior of a fiber end in short fiber reinforced composites

Progress in Complex 2d and 3d Cohesive Fracture Modelling Considering Random Heterogeneity

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Photoelastic Investigation of Interaction Between Matrix Crack and Different Shapes of Inclusions

Finite Element Analysis of Matrix Crack Deflection Mechanisms in Fiber-Reinforced Composites

Analytical and Numerical Analyses for a Penny-Shaped Crack Embedded in an Infinite Transversely Isotropic Multi-Ferroic Composite Medium: Semi-Permeable Electro-Magnetic Boundary Condition

Study on Crack-Inclusion Interaction Using Digital Gradient Sensing Method

Mixed Scheme of the Finite Element Method as a Basis for Computational Analysis of Model Crack Mechanics Problems

Crack–inclusion interaction in a quasicrystal medium with nonlocal effect

Multilayered piezomagnetic/piezoelectric composites with periodic interfacial cracks subject to in-plane loading

A General Property-Structure Relationship from Crack Stability Analysis on Hybrid Staggered Composites with Elasto-Plastic Matrices

A Monte Carlo simulation of damage and failure process with crack saturation for unidirectional fiber reinforced ceramic composites

A novel phase‐field based cohesive zone model for modeling interfacial failure in composites

A phase-field fracture model for fatigue behavior in fiber-reinforced composites

Mechanical and Fracture Behaviors of Brittle Material with a Circular Inclusion: Insight from Infilling Composition

STUDY OF CONCRETE FRACTURE PROCESS ZONE BASED ON FICTITIOUS CRACK MODEL

A Study on Phase-Field Models for Brittle Fracture

A Microscopic Elasto-Plastic Damage Model for Characterizing Transverse Responses of Unidirectional Fiber-Reinforced Polymer Composites

The mechanics of matrix cracking in brittle-matrix fiber composites

Crack-tip Fields of an Anti-Plane Crack in Micropolar Elastic Solids