Abstract:We designed a hydrogel with durable and excellent antibacterial activity. Amphiphilic block copolymer, polycaprolactone-block-poly(glutamic acid) (PCL-b-PGA), was first synthesized by ring-opening polymerization with amine-terminated polycaprolactone (PCL-NH2 ) as the macro-initiator and Bz-Glu-NCA as the monomer. This copolymer self-assembled into vesicles in solvent mixture of DMF/water with a critical vesiculation concentration of 5.27 mu g mL(-1). Antibacterial Ag-decorated vesicles were then prepared by in situ deposition of silver nanoparticles in PGA coronas of the vesicles as a result of the electrostatic interaction between carboxyl groups and Ag+ H-1-NMR analysis revealed the composition of PCL47-b-PGA(46) block copolymer. Dynamic light scattering (DLS) study revealed an intensity-averaged diameter of 215 nm for the vesicles with a polydispersity of 0.029. Transmission electron microscopy (TEM) confirmed a hollow structure of the vesicles with a number-averaged diameter of 270 nm, and the presence of sliver nanoparticles on the vesicles. Atomic force microscopy (AFM) revealed the collapsed surface morphology of vesicles with a width to height ratio of 18, confirming further the hollow structure of the vesicles. Meanwhile, Ag-decorated vesicles were incoporated into Pluronic F127 hydrogels to afford antibacterial hydrogels, showing good degradability at different pH. MIC90 (minimum concentration of inhibiting 90% of bacterium) of the antibacterial vesicles was 10 mu g mL(-1) against Gram-negative bacterium E. coli, and it was 20 mu g mL(-1) against Gram-positive bacterium S. aureus, and measured by spread plate method, which afford the hydrogels excellent antibacterial property. Oxford cup tests confirmed that MIC50 of the antibacterial hydrogel against both E. coli and S. aureus is 7.5 mu g mL(-1) and MBC (minimum bactericidal concentration) against both of them is 30 mu g mL(-1). The in vitro degradation tests confirmed that the vesicle was degraded in the presence of lipase. Overall, we provide a new method for preparation of antibacterial hydrogels, which may have promising biomedical applications requiring a long-acting antibacterial therapy such as inflammation triggered by bacteria infection, wound healing after surgery and sterilization for the implant devices, etc.

Synthesis and Properties of the Antibacterial Hydrogels with Enhanced Mechanical Strengths

Novel Complex Hydrogels Based on N-carboxyethyl Chitosan and Quaternized Chitosan and Their Controlled in Vitro Protein Release Property.

Preparation of Antimicrobial PHEMA-g-PCBMAE Hydrogels with Improved Mechanical Properties

Synthesis And Drug-Release Studies Of Low-Fouling Zwitterionic Hydrogels With Enhanced Mechanical Strength

Preparation of Antimicrobial Polycarboxybetaine‐based Hydrogels for Studies of Drug Loading and Release

Synthesis of Cationic Hydrogels with Tunable Physicochemical Properties for Antibacterial Applications

Synthesis of Cellulose-Based Double-Network Hydrogels Demonstrating High Strength, Self-Healing, and Antibacterial Properties.

Preparation of cationic polyelectrolyte grafted polyvinyl alcohol-formaldehyde macroporous hydrogels and their antibacterial properties

Construction and characterization of chitosan/poly(acrylamide-[2-(methacryloyloxy)ethyl]trimethylammonium chloride) double-network hydrogel with enhanced antibacterial activity

Tough complex hydrogels transformed from highly swollen polyelectrolyte hydrogels based on Cu2+ coordination with anti-bacterial property

Poly(hexamethylene Guanidine)‐based Hydrogels with Long Lasting Antimicrobial Activity and Low Toxicity

Tough Complex Hydrogels Transformed from Highly Swollen Polyelectrolyte Hydrogels Based on Cu2+ Coordination with Anti-Bacterial Properties.

UV-Cured Antibacterial Hydrogels Based on PEG and Monodisperse Heterofunctional Bis-MPA Dendrimers

Antibacterial Hydrogels Incoporated with Poly(glutamic acid)-based Vesicles

Antibacterial Poly(ethylene Glycol) Hydrogels from Combined Epoxy‐amine and Thiol‐ene Click Reaction

Preparation and characterization of carboxymethyl chitosan/polyvinyl alcohol composite hydrogel with improved mechanical and antibacterial properties

Charged group-modified poly(vinyl alcohol) hydrogels: Preparation and antibacterial property

A Novel Multifunctional Crosslinking PVA/CMCS Hydrogel Containing Cyclic Peptide Actinomycin X2 and PA@Fe with Excellent Antibacterial and Commendable Mechanical Properties

Ultra-high Strength Poly(n-(2-hydroxyethyl)acrylamide)/chitosan Hydrogel with "repelling and Killing" Bacteria Property.

Ε-Poly(l-lysine)-based Hydrogels with Fast-acting and Prolonged Antibacterial Activities

Uniform antibacterial cylindrical nanoparticles for enhancing the strength of nanocomposite hydrogels