Spectroscopy and Energy Transfer Dynamics of Nd3+ Strengthened Er3+: 2.7 Μm Emission in Modified Fluoride Glass

Liyan Zhang,Binhua Yang,Lili Hu
DOI: https://doi.org/10.1016/j.jqsrt.2014.05.004
2014-01-01
Abstract:A modified fluoride glass with high Tg (453°C) and Txonset–Tg(138°C) value was studied as the Er3+:Nd3+ codoped 2.7µm gain media. Interestingly, Nd3+: 1600nm absorption band that never been reported in glass material was observed. This band induces efficient non-phonon-assisted de-sensitization process in Er3+: 2.7µm emission. Surprisingly, a strong 817nm peak was detected, which is proved to be induced by the cross-relaxation process based on the Nd3+:4I15/2 level, making the energy back-transfer from Nd3+ to Er3+ possible. Results show that Nd3+ strengthens the Er3+: 2.7µm emission significantly, but energy transfer coefficient from Er3+ to Nd3+ increases greatly with Nd3+ enhancement, leading to more complicated inter-ionic interactions and more energy loss. Low Nd3+:Er3+ ratio is preferred to achieve strong 2.7µm emission, meanwhile, suppressing upconversion luminescence, weakening the Nd3+ interactions and decreasing the thermal load of 2.7µm lasing effectively.
What problem does this paper attempt to address?