Study on physicochemical mechanism of nickel surface oxidation behavior under high temperature condition by using molecular dynamic method
X. Lu,T. Ma,M. Zeng,Y. Chen,Q. W. Wang
2015-01-01
Abstract:The surface oxidation problem of structure materials in high temperature facilities is primarily important since it is responsible for the deterioration of material properties during their service lives in engineering. This paper mainly focuses on the fundamental high temperature oxidation problem by employing reactive molecular dynamic (MD) method. The simulated oxidation reaction processes are on different nickel crystallographic orientations including Ni (001), Ni (110) and Ni (111) surfaces. The simulated exposure temperature conditions ranges from 900 K to 1500 K. Also, two different oxygen pressure conditions P0 and 2P0 are calculated under 900 K and 1200 K to check the oxygen pressure effect on surface oxidation problem. All the above cases are calculated as long as 1000 ps (1 ns). The results of atomistic scale simulations reveal that higher exposure temperature and larger oxygen pressure lead to greater amount of oxide formed on nickel surfaces but the rate of increase is dependent on surface orientation. Also, atomic scale comparison between iron and nickel oxidation dynamics under 900 K shows that iron has about 6.9 times of oxide formed than nickel in the present simulated conditions. INTRODUCTION High temperature heat exchangers are required in many industrial systems for process reasons or aiming to attain high efficiency. Among these, the most promising fields are recuperative gas turbine and combined cycles, recuperative microturbine systems and external combustion gas turbine. The innovative solutions for high temperature heat exchanger lies on several vital aspects, including high temperature compact heat exchangers structure, thermo-fluid dynamic technology and corrosion resistance of materials. For the first two parts, thermal scientists have investigated abundantly, either from the compact innovative flow passages such as primary surface recuperator, plate-fin heat exchangers as well as printed circuit heat exchangers or to the thermo-hydraulic characteristics of supercritical CO2 working fluids (Xu et al., 2014). However, the good corrosion/oxidation resistance and mechanical properties of structure material play a fundamental role for the facilities’ safe and reliable performance under severe environments such as corrosive, high temperature, high pressure, irradiative, etc. High temperature corrosion/oxidation of metal has long been a problem since industrial revolution emerged. Different species of metal combined with various kinds of corrosive agent make it rather complex to understand the corrosion mechanisms. For the engineering situations such as microturbine systems, gas fuels are clean working fluids without too much kinds of impurity oxidant. Hence, oxygen becomes primary attacking oxidising species during high temprature process. In terms of the state of understanding on high temperature oxidation, a large amount of works have been implemented by experimental and theoretical methods to grasp the mechanisms of high temperature oxidation for metal. The diffusion coefficient of oxygen with metal elements such as Ni has been experimentally measured by scientists including Atkinson et al. (1986). Kinetic growth of oxidation layer has been investigated by both high temperature metal oxidation theory (Wagner, 1973) and experimental investigation. A comprehensive review on diffusion coefficient for nickel and oxygen and oxidation kinetic theories and experiment data could be found in Li (2001)’s literature. Micro-scale processes including metal ion diffusion and oxygen diffusion process as well as bond breaking/combination are of primary importance to explain physical phenomenon such as oxidation or changes in mechanical properties. But these small scale phenomenons are not easy to observe. Thanks to the raise of atomic-scale computational science, atomic-scale mechanisms of metal oxidation problem can be solved with the aid of simulation method. Papageorgiou et. al. (2002) used the rigid iron potential model to simulate the oxygen adatom (O) diffusion on the NiO(001) surface. Vesel et. al. (2002) presented the MD simulation results on the processes happening upon deposition of oxygen ions on the NiO(001) surface to Proceedings of International Conference on Heat Exchanger Fouling and Cleaning 2015 (Peer-reviewed) June 07 12, 2015, Enfield (Dublin), Ireland Editors: M.R. Malayeri, H. Müller-Steinhagen and A.P. Watkinson Published online www.heatexchanger-fouling.com