Abstract:Purpose This paper aims to investigate the effect of alternating current (AC) on corrosion, it is not yet clear about the exact mechanism of the corrosion induced by AC. Previous reports indicated that AC corrosion was similar to the effect of continuous cathodic and anodic polarization on the corrosion process of the metals. Wan et al. studied the effect of negative half-wave AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in near-neutral solution. Design/methodology/approach This study attempted to understand the AC-induced corrosion by imposing the half-cycle AC on the X80 pipeline steel in an acid bicarbonate solution. The AC corrosion mechanism was determined by weight loss and potentiodynamic polarization curve measurements, as well as surface characterization. Findings The results show that the positive half-cycle AC accelerated the uniform corrosion in the NaHCO3 solution, the negative half-cycle AC would decrease the uniform corrosion and local corrosion was increased and some Ca and Mg deposited on the surface of X80 steel, so the corrosion rate decreased by negative half-cycle AC. The corrosion product was composed of α -FeOOH under the application of positive half-cycle AC. The oxygen reduction led to a local increase of pH near the electrode surface and led to the formation of α -FeOOH, which enhanced the protectability of corrosion products. Originality/value Researchers studied the effect of negative half-wave AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in near-neutral solution. However, the AC behavior and corrosion mechanism in acid solution are unknown. So to make clear about the corrosion behavior of metals in different polarization states and the mechanism involved, diode technology was used to research the AC corrosion, half-wave AC was applied on the metals after the full-wave rectified.

Effect of Alternating Voltage on Corrosion of X80 and X100 Steels in a Chloride Containing Solution – Investigated by AC Voltammetry Technique

X80 Steel Corrosion Induced by Alternating Current in Water-Saturated Acidic Soil

Influence of alternating current on corrosion behavior of X100 steel in Golmud soil simulated solution with different pH

The influence of half-cycle rectified sinusoidal alternating current (AC) on corrosion of X80 pipeline steel in an acid bicarbonate solution

Effect of Alternating Current on Passive Film and Corrosion Behavior of Pipeline Steel with Different Microstructures in Carbonate/Bicarbonate Solution

Galvanic Effect and Alternating Current Corrosion of Steel in Acidic Red Soil

Effect of pH value on corrosion of carbon steel under an applied alternating current

Influence of Alternating Voltages on Passivation and Corrosion Properties of X80 Pipeline Steel in High Ph 0.5 Mol L− 1nahco3+0.25 Mol L− 1Na2co3solution

Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment

Comparison of Synergistic Effect of Counterions on Corrosion Inhibition of Mild Steel in Acid Solution: Electrochemical, Gravimetric and Thermodynamic Studies

Study on the Corrosion Behavior and Mechanism of 6061 Aluminum Alloy under Alternating Current Interference in 3.5% NaCl Solution

Electrochemical Investigation Of Corrosion Of X80 Steel Under Elastic And Plastic Tensile Stress In Co2 Environment

The Corrosion Behavior of Carbon Steel in CO2‐saturated NaCl Crevice Solution Containing Acetic Acid

Influence of the cathodic charging current on electrochemical behaviors of X80 steel in an simulated acidic soil solution

Research on AC corrosion behavior and corrosion product film evolution of X70 steel under the combined action of AC interference and CP

EFFECT OF CHLORIDE ION ON CORROSION BEHAVIOR OF N80 STEEL IN CO2 SOLUTIONS

Galvanic Corrosion Behavior of 13Cr-N80 Steel Couples in NaCl Solution with Different Concentrations

The influence of tensile stress on the electrochemical behavior of X80 steel in a simulated acid soil solution

AC corrosion behavior and the effect of stone-hard-soil on corrosion process in the earth alkaline rich environment

Effect of Microstructures on Corrosion of X80 Pipeline Steel in an Alkaline Soil

Relationship Between Dissolved Oxygen and Corrosion Characterization of X80 Steel in Acidic Soil Simulated Solution