Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

In Situ Corrosion Characterization of Simulated Weld Heat Affected Zone on API X80 Pipeline Steel

Corrosion characteristics of simulated reheated heat-affected-zone of X80 pipeline steel in carbonate/bicarbonate solution

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Corrosion behavior of the weld joint of X80 pipeline steel in an acidic red soil

Internal localized corrosion of X100 pipeline steel under simulated flow conditions

Corrosion behaviour of X80 pipeline steel welded joint in H2O- saturated supercritical-CO2 environment

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film

Study on metal corrosion behavior of heat-affected zone of oil pipeline

Study on Corrosion Behavior of X80 Pipeline Steel in 5%NaCl+0.5% Acetum

Stress-Corrosion-Cracking Sensitivity of the Sub-Zones in X80 Steel Welded Joints at Different Potentials

Electrochemical Investigation of the Corrosion Behavior of API 5L-X65 Carbon Steel in Carbon Dioxide Medium

CO2 corrosion behavior of simulated heat-affected zones for X80 pipeline steel

Anodic Dissolution Characteristics of the X80 Pipeline Steel in Simulated Soil Solution

Changes in microstructure and properties of weld heat-affected zone of high-strength low-alloy steel

Technical Note: Study on Accelerated Corrosion Behavior and Mechanism of X80 Pipeline Steel Welded Joint under Cyclic Salt Spray Test

Electrochemical and Mechanical Properties of Cathodically Protected X80 Steel in Different Temperature Soil

Corrosion behavior study on heat treated API X70 pipeline steel exposed in different aggressive environments

Study on accelerated corrosion behavior and mechanism of X80 pipeline steel welded joint under cyclic salt spray test

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

STUDY ON THE ACCELERATED CORROSION BEHAVIOR OF A GALVANIZED X80 PIPELINE STEEL WELDED JOINT DURING A CYCLIC SALT SPRAY TEST

The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements