Effect of Nb on Hydrogen-Induced Delayed Fracture in High Strength Hot Stamping Steels

Shiqi Zhang,Yunhua Huang,Bintang Sun,Qingliang Liao,Hongzhou Lu,Bian Jian,Hardy Mohrbacher,Wei Zhang,Aimin Guo,Yue Zhang

DOI: https://doi.org/10.1016/j.msea.2014.12.051

IF: 6.044

2015-01-01

Materials Science and Engineering A

Abstract:The effect of Nb addition (0.022, 0.053, 0.078 wt%) on the hydrogen-induced delayed fracture resistance of 22MnB5 was studied by constant load test and electrochemical hydrogen permeation method. It is shown that the appropriate addition of Nb is beneficial to the improvement of the delayed fracture resistance of tested steel, especially when the steel contains high concentration of hydrogen, and the maximum delayed fracture resistance is obtained at a Nb content of 0.053%.The result of hydrogen permeation test shows that the diffusion coefficient of hydrogen in the steel containing niobium is lower than that in steel without niobium, which indicates that it is harder for hydrogen in the steels containing niobium to diffuse and aggregate. In addition, the reason for Nb improving the delayed fracture resistance of steels is discussed from two aspects: hydrogen trap effect and grain refinement effect. The analysis shows that the main reason leading to the improvement of the delayed fracture resistance is the hydrogen trapping effect of NbC while the grain refinement effect of Nb(C,N) secondary.