Microstructure and Mechanical Properties of Weld-Bonded and Resistance Spot Welded Magnesium-to-steel Dissimilar Joints

W. Xu,D. L. Chen,L. Liu,H. Mori,Y. Zhou

DOI: https://doi.org/10.1016/j.msea.2011.12.096

IF: 6.044

2012-01-01

Materials Science and Engineering A

Abstract:The aim of this study was to evaluate microstructures, tensile and fatigue properties of weld-bonded (WB) magnesium-to-magnesium (Mg/Mg) similar joints and magnesium-to-steel (Mg/steel) dissimilar joints, in comparison with resistance spot welded (RSW) Mg/steel dissimilar joints. In the WB Mg/Mg joints, equiaxed dendritic and divorced eutectic structures formed in the fusion zone (FZ). In the dissimilar joints of RSW and WB Mg/steel, FZ appeared only at Mg side with equiaxed and columnar dendrites. At steel side no microstructure changed in the WB Mg/steel joints, while the microstructure in the RSW Mg/steel joints consisted of lath martensite, bainite, pearlite and retained austenite leading to an increased micro-hardness. The relatively low cooling rate suppressed the formation of shrinkage porosity but promoted the formation of MgZn2 and Mg7Zn3 in the WB Mg/steel joints. The added adhesive layer diminished stress concentration around the weld nugget. Both WB Mg/Mg and Mg/steel joints were significantly stronger than RSW Mg/steel joints in terms of the maximum tensile shear load and energy absorption, which also increased with increasing strain rate. Fatigue strength was three-fold higher for WB Mg/Mg and Mg/steel joints than for RSW Mg/steel joints. Fatigue failure in the RSW Mg/steel joints occurred from the heat-affected zone near the notch root at lower load levels, and in the mode of interfacial fracture at higher load levels, while it occurred in the Mg base metal at a maximum cyclic load up to similar to 10 kN in both WB Mg/Mg and Mg/steel joints. (C) 2011 Elsevier B.V. All rights reserved.