Abstract:A series of radiopaque polyurethanes used for prosthetic disc nucleus were prepared via polycondensation between polyurethane prepolymer and N,N′-bis(1,3-dihydroxypropyl)-2,3,5,6-tetra iodoterephthalamide(BDTIP),which was synthesized as crosslinker and X-ray contrast agent.The structure of BDTIP was characterized by 1H-NMR.Infrared spectroscopy was used to monitor the reaction degree of BDTIP.The developing effect of modified polyurethane was characterized by X-radiography.Meanwhile,the cytotoxicity was tested by the method of thiazolyl blue tetrazolium bromide(MTT) colorimetric assay using mouse fibroblast,and the mechanical properties of radiopaque polyurethanes with different iodine contents were also studied.The results of 1H-NMR showed that the hydrogen atoms on benzene ring were replaced by iodine completely and expected structure was obtained.Polyether polyurethane structure,demonstrated by FTIR,was also obtained.The X-radiography results showed that polymer had a good radiopacity which is almost equivalent to that of a 2 mm thick aluminum wedge when the iodine content was very small,while the mechanical properties were still excellent.There was nearly no change of compression modulus when the iodine content is low and within half an hour after the compression test the shape of prosthetic disc nucleus were restored to the state before compression,which demonstrated that the addition of BDTIP had little effect on the mechanical properties of prosthetic disc nucleus of polyurethane.The cell proliferation rate(RGR) of all modified polyurethanes was more than 75%,they were all biomaterials without cytotoxicity.This study provides a new modification way for preparing radiopaque polyurethane used for prosthetic disc nucleus.

Radiopaque Polyurethanes with Flexible Iodine-Containing Chain Extender

Synthesis And Characterization Of Radiopaque Poly(Ether Urethane) With Iodine-Containing Diol As Chain Extender

Radiopaque iodinated polyurethane for embolic agents

Enzymatic degradation and radiopaque attenuation of iodinated poly(ester-urethane)s with inherent radiopacity

Biodegradable Radiopaque Iodinated Poly(ester Urethane)s Containing Poly(ε‐caprolactone) Blocks: Synthesis, Characterization, and Biocompatibility

PREPARATION AND PROPERTIES OF A NEW RADIOPAQUE POLYURETHANES

Radiopaque Iodinated Poly(ester-Urethane)s Based on Poly(butylene Succinate): Retarded Crystallization and Dual Recrystallization Behaviour

Design and Synthesis of Novel Iodinated Polycarbonates with Inherent X-Ray Opacity

Radiopaque Polyurethanes Containing Barium Sulfate: A Survey on Thermal, Rheological, Physical, and Structural Properties

Synthesis and Characterization of Novel Radiopaque Polycarbonate

Iodinated Poly(p-Dioxanone) As a Facile Platform for X-ray Imaging of Resorbable Implantable Medical Devices.

Synthesis and characterization of thermally stable poly(urethane-imide)s based on novel diols-containing imide and alkynyl groups

Ultra-tough Light-Curing Ionogels for UV Shielding

STUDY OF BODY TEMPERATURE CURABLE AND RADIOPAQUE POLYURETHANE FOR PROSTHETIC DISC NUCLEUS

Synthesis and Characterization of Poly(imide‐urethane) Based on Novel Chain‐extender Containing Both Imide and Sulphone Functions

Synthesis and Characterization of Inherently Flame‐retardant and Anti‐dripping Thermoplastic Poly(imides‐urethane)s

Synthesis of non‐isocyanate polyurethanes with high‐performance and self‐healing properties

Construction of hydroxyl-functionalized hyper-crosslinked networks from polyimide for highly efficient iodine adsorption

Preparation of Polyurethane Ionomers by Reactive Extrusion and Dispersions Containing Sulfonate Groups and Polyethylene Glycol Segments

Biooxazolidines‐enabled Improvement of Monocomponent Polyurethane Coatings

Chain‐extended Polyurethane–acrylate Ionomer for UV‐curable Waterborne Coatings