Tetradecanol/expanded graphite composite form-stable phase change material for thermal energy storage

julan zeng,juan gan,furong zhu,saibo yu,zhongliang xiao,wenpei yan,ling zhu,zhenqiang liu,lixian sun,zhong cao
DOI: https://doi.org/10.1016/j.solmat.2014.04.015
IF: 6.9
2014-01-01
Solar Energy Materials and Solar Cells
Abstract:Natural flake graphite was chemically intercalated to prepare expandable graphite. The expandable graphite was then expanded by means of microwave irradiation to obtain expanded graphite (EG). Tetradecanol (TD)/EG composite form-stable phase change materials (PCMs) were prepared by mixing TD with EG through an autoclave method. The highest loading of TD in the composite form-stable PCMs with good form-stability was 93wt%. The composite form-stable PCMs exhibited excellent thermal energy storage capacity. The melting enthalpy (ΔHm) and crystallization enthalpy (ΔHc) of the composite form-stable PCM containing 93wt% TD were 202.6 and 201.2J/g, respectively. However, the solid–solid phase transition of TD in the composite form-stable PCMs was hindered as TD was strongly absorbed by EG. As a result, the ΔHm and ΔHc of the composite form-stable PCMs were slightly lower than the theoretical value. The thermal conductivity of the composite form-stable PCMs was greatly enhanced by EG and was increased with the increasing of EG loading. The thermal conductivity of the composite form-stable PCM containing 7wt% EG attained 2.76W/mK. Besides, effects of the prepared EG on properties of the composite form-stable PCMs were compared with those of EG derived from commercially obtained expandable graphite.
What problem does this paper attempt to address?