Abstract:We report a synthesis method for highly monodisperse Cu-Pt alloy nanoparticles. Small and large Cu-Pt particles with a Cu/Pt ratio of 1:1 can be obtained through colloidal synthesis at 300 °C. The fresh particles have a Pt-rich surface and a Cu-rich core and can be converted into an intermetallic phase after annealing at 800 °C under H2. First, we demonstrated the stability of fresh particles under redox conditions at 400 °C, as the Pt-rich surface prevents substantial oxidation of Cu. Then, a combination of in situ scanning transmission electron microscopy, in situ X-ray absorption spectroscopy, and CO oxidation measurements of the intermetallic CuPt phase before and after redox treatments at 800 °C showed promising activity and stability for CO oxidation. Full oxidation of Cu was prevented after exposure to O2 at 800 °C. The activity and structure of the particles were only slightly changed after exposure to O2 at 800 °C and were recovered after re-reduction at 800 °C. Additionally, the intermetallic CuPt phase showed enhanced catalytic properties compared to the fresh particles with a Pt-rich surface or pure Pt particles of the same size. Thus, the incorporation of Pt with Cu does not lead to a rapid deactivation and degradation of the material, as seen with other bimetallic systems. This work provides a synthesis route to control the design of Cu-Pt nanostructures and underlines the promising properties of these alloys (intermetallic and non-intermetallic) for heterogeneous catalysis.

ChemInform Abstract: Solid Phase Metallurgy Strategy to Sub‐5 Nm Au—Pd and Ni—Pd Bimetallic Nanoparticles with Controlled Redox Properties.

Solid Phase Metallurgy Strategy to Sub-5 Nm Au-Pd and Ni-Pd Bimetallic Nanoparticles with Controlled Redox Properties.

Enhancing the Catalytic and Electrocatalytic Properties of Pt-based Catalysts by Forming Bimetallic Nanocrystals with Pd

Trimetallic PtPdCo Mesoporous Nanopolyhedra with Hollow Cavities

Control over the Morphology and Plasmonic Properties of Rod-like Au-Pd Bimetallic Nanostructures

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

A General Strategy Assisted with Dual Reductants and Dual Protecting Agents for Preparing Pt-Based Alloys with High-Index Facets and Excellent Electrocatalytic Performance.

Synthesis and Characterization of Stable Cu-Pt Nanoparticles under Reductive and Oxidative Conditions

Structural Optimization and Melting Behavior Investigation of Pd-Ag Bimetallic Nanoparticles by Molecular Simulations

Facile Synthesis of Highly Dispersed and Well‐Alloyed Bimetallic Nanoparticles on Oxide Support

Microfluidic-enabled ambient-temperature synthesis of ultrasmall bimetallic nanoparticles

Synthesis of Au-Ni Bimetallic Nanoparticles with Tunable Aspect Ratio

Temperature-driven phase transformation and element segregation in Pd-Ru immiscible alloy nanoparticles: Spatial resolving of elements and insights for electrocatalysis

Synthesis of thermally stable and highly active bimetallic Au-Ag nanoparticles on inert supports

Pd–Pt Nanoalloy Transformation Pathways at the Atomic Scale

Synthesis and Characterization of Cu-Pt Bimetallic Nanoparticles

Poly(N‐Heterocyclic Carbene)‐Capped Alloy and Core‐Shell AuAg Bimetallic Nanoparticles

Bimetallic Pd-Cu nanocrystals and their tunable catalytic properties.

Breaking with the Principles of Coreduction to Form Stoichiometric Intermetallic PdCu Nanoparticles

Surface Faceting and Compositional Evolution of Pd@ Au Core- Shell Nanocrystals During in Situ Annealing

Palladium/tin Bimetallic Single-Crystalline Hollow Nanospheres