Abstract:A facile method for the synthesis of size- and shape-controlled CuTnS(2) semiconductor nanocrystals was developed by thermolysis of a mixed solution of CuAc. In(Ac)(3) (molar ratio of CuAc to In(Ac)(3) = 1: 1) and dodecanethiol in noncoordinating solvent 1-octadecene (ODE) at 240 degrees C. CuInS2 nanoparticles with size of 2 to similar to 5 nm and nanorods with aspect ratio of 1 to similar to 3 were obtained by adjusting the reaction parameters such as temperature and time. The as-prepared nanoparticles were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy, selected area electron diffraction spectroscopy, inductively Coupled plasma atomic emission spectroscopy, UV-vis absorption, and photoluminescence (PL) spectroscopy. The nanoparticle solutions exhibit tunable absorption and PL spectra with the absorption edge ranging from 550 to 750 nm and PL emission peaks from 600 to 750 rim, indicating a strong size-dependent quantum confinement effect. Optical measurements of the CuInS2) nanoparticles demonstrated that their optical properties are related to donor-acceptor defects, size-dependent quantum confined effects. and surface defects. The PL decay curve of CuInS2 nanoparticles has a triple exponential characteristic with lifetimes of 4-12. 28-60, and 140-300 ns, respectively, and the PL emission with the longest lifetime (140-300 ns) Occupied 40-80% of the PL emission of the samples. These results imply that the room-temperature PL emission of CuInS2 nanoparticles involves three types of recombination: band exciton recombination, surface-related recombination, and donor-acceptor defects recombination. Among them, the PL emission from donor-acceptor defects occupied a large amount.

ChemInform Abstract: Controlled Synthesis and Optical Properties of Colloidal Ternary Chalcogenide CuInS2 Nanocrystals.

Controlled Synthesis of Luminescent Cuins2 Nanocrystals and Their Optical Properties

ChemInform Abstract: Controlled Synthesis and Optical Properties of Colloidal Ternary Chalcogenide CuInS2 Nanocrystals.

Shape- and Phase-Controlled Synthesis of Monodisperse, Single-Crystalline Ternary Chalcogenide Colloids Through A Convenient Solution Synthesis Strategy

Colloidal synthesis of monodisperse quaternary CuInSSe nanocrystals

Tunable Optical Properties of Ternary Non‐stoichiometric Cu–In–S Nanocrystal Emitters

Synthesis and hybridization of CuInS2 nanocrystals for emerging applications

Facile synthesis and characterization of CuInS2 nanocrystals with different structures and shapes

Optical and Optoelectrical Properties of Ternary Chalcogenide CuInS2/TiO2 Nanocomposite Prepared by Mechanochemical Synthesis

Formation of High-Quality I-Iii-Vi Semiconductor Nanocrystals by Tuning Relative Reactivity of Cationic Precursors

Colloidal CuInSe2 Nanocrystals in the Quantum Confinement Regime: Synthesis, Optical Properties, and Electroluminescence

Shape-Controlled Synthesis of Ternary Chalcogenide ZnIn2S4 and CuIn(S,Se)2 Nano-/Microstructures Via Facile Solution Route

One-pot Synthesis of CuInS2 Nanocrystals Using Different Anions to Engineer Their Morphology and Crystal Phase.

New Insights Into The Formation And Color-Tunable Optical Properties Of Multinary Cu-In-Zn-Based Chalcogenide Semiconductor Nanocrystals

Synthesis and Characterization of Highly Luminescent CuInS2 and CuInS2/ZnS (core/shell) Nanocrystals

Synthesis of CuInSe_2 Nanocrystals

One-Step Synthesis of Near-Infrared Emitting and Size Tunable Cuins2 Semiconductor Nanocrystals by Adjusting Kinetic Variables

Synthesis of Cu-In-S ternary nanocrystals with tunable structure and composition.

Controlled Synthesis of Wurtzite CuInS2 Nanocrystals and Their Side-by-side Nanorod Assemblies

Magnetically-induced Synthesis of Highly-Crystalline Ternary Chalcopyrite Nanocrystals under Ambient Conditions

Solvothermal Synthesis and Characterization of Chalcopyrite CuInSe2 Nanoparticles