Abstract:The effect of ZnO on the crystal structure, sintering behavior, and electrical conductivity of yttrium-doped BaCeO3-BaZrO3 was investigated by unfixing or fixing the yttrium content noted as BaCe0.5Zr0.3Y0.2-xZnxO2.9-0.5x and BaCe0.5Zr0.3Y0.2O2.9+yZnO, respectively. Studies on the two series revealed that BaO center dot ZnO eutectic, rather than ZnO, was responsible for the sintering densification. For BaCe0.5Zr0.3Y0.2-xZnxO2.9-0.5x, the evaporation of ZnO center dot BaO eutectic was observed after sintering at 1300 degrees C for 10 h, and few impurities were detected by XRD with x < 0.20. For BaCe0.5Zr0.3Y0.2O2.9+yZnO, the concomitant loss of BaO with ZnO caused A-site deficiency and led to impurities of Y2O3 for y=0.08 and 0.14, and Y2BaZnO5 for y=0.20 during the sintering. For both series, ZnO enhanced the relative density, which was above 97% with x or y varying from 0.02 to 0.08. Energy-dispersive X-ray spectroscopy analysis revealed that ZnO hardly entered the perovskite phase. The conductivity study also suggested that ZnO did not serve as a dopant and that yttrium content was essential for sustaining a high ionic conduction. Excessive ZnO was especially detrimental to the grain boundary conduction and thus lowered the total electrical conduction. The optimized composition of BaCe0.5Zr0.3Y0.2O2.9+0.04ZnO has been obtained, with both a high relative density (similar to 98.5%) and a high electrical conductivity (1.35 x 10-2 S/cm at 600 degrees C).

Structure and Electrical Conductivity of BaCe0.7In0.1A0.2O3−δ (A = Gd, Y) Ceramics

Thermal Conductivity and Expansion Coefficient of (Sm0.5Gd0.3Yb0.2)2Ce2O7

Structure and Electrical Conductivity of BaCe0.85Ln0.15O3−δ (ln=gd, Y, Yb) Ceramics

Synthesis, Structure and Electrical Conductivity of BaZr1–xDyxO3–δ Ceramics

Preparation, Structure and Electrical Conductivity of Pyrochlore-Type Gd1−xEu2xSm1−xZr2O7 Ceramics with a Constant Lattice Parameter

Sintering, chemical stability and electrical conductivity of the perovskite proton conductors BaCe0.45Zr0.45M0.1O3-δ (M = In, Y, Gd, Sm)

Electrical Conductivity of 5 Mol.% Yb2o3 and 5 Mol.% Gd2o3 Co-Doped Sm2zr2o7

In situ XPS and impedance spectroscopy studies of (1 − x)Ba0.5Bi0.5FeO3 − xGd2O3 ceramics with negative temperature coefficient

Ionic Conductivity, Sintering and Thermal Expansion Behaviors of Mixed Ion Conductor BaZr0.1Ce0.7Y0.1Yb0.1O3−δ Prepared by Ethylene Diamine Tetraacetic Acid Assisted Glycine Nitrate Process

Structure and Thermal Conductivity of Gd2(TixZr1−x)2O7 Ceramics

Investigation of electrical conductivity and oxygen relaxation behavior for BaBi0.98Sr0.02Nb5-xTixO15-δ ceramics

Effect of Sm Substitution for Gd on the Electrical Conductivity of Fluorite-Type Gd2Zr2O7

Structural, thermal, and electrical properties of A-site double-lanthanide La1-Gd BaCo2O5+ ceramics

Effect of CaO addition on the structure and electrical conductivity of the pyrochlore-type GdSmZr2O7

Thermoelectric performance of textured Ca3−xYbxCo4O9−δ ceramics

Conductivity of Bi-Doped Ba0.6Sr0.4CeO3 Electrolyte Materials

The Influence of Doping Ta on the Properties of BaCe0.8In0.1Y0.1O3-δ Electrolyte

Synthesis and characterization of CaZr0.95In0.05O3 − δ–BaCe0.9Y0.1O3 − θ composite ceramics

Electrical Conductivity of Nd and Ce Co-Doped Gd2zr2o7 Ceramics

Sintering behavior and conductivity study of yttrium-doped BaCeO 3-BaZrO3 solid solutions using ZnO additives

Structure, electrical and thermal properties of (Ba 0.5Sr 0.5) 1 - XGd xCo 0.8Fe 0.2O 3-δ perovskite as a solid-oxide fuel cell cathode