Abstract:NiO nanomaterials prepared using a solid–liquid NH3·H2O precipitation method (NiO-NSL) were tested in the catalytic combustion of methane. The NiO-NSL presented a characteristic rod-like nanostructure with a length of about a few hundred nanometers except for a part of the nanoparticles. For comparison, the NiO nanomaterials prepared by the traditional liquid-phase NH3·H2O precipitation method (NiO-NLL) were tested in the same reaction conditions. NiO-NSL exhibited significantly higher methane combustion activity than NiO-NLL and achieved the complete combustion of methane at 390 °C, which was outstanding in non-noble metal-based catalyst. X-ray photoelectron spectroscopy (XPS) and hydrogen-temperature-programmed reduction (H2-TPR) results indicate that the surface Ni2+ content of NiO-NSL was higher than that of NiO-NLL, and the presence of more Ni2+ might be responsible for the enhanced activity. DFT calculations prove that the energy barrier for C–H bond activation on Ni2+ was lower than that on Ni3+, which was consistent with the higher methane catalytic combustion activity of NiO-NSL. In addition, when the precipitating agent was replaced with NaOH and (NH4)2CO3, the generalization of the solid–liquid precipitation method in the preparation of the NiO catalysts was also tested. The results show that the solid–liquid precipitation method proposed in this work was still applicable when NaOH was used as a precipitant. However, with the use of (NH4)2CO3 as a precipitant, the methane catalytic activity of the NiO nanoparticles prepared by the solid–liquid precipitation method was reduced to a certain extent compared with the traditional liquid-phase precipitation method. This research can open up a highly efficient and environmentally friendly method for the synthesis of methane combustion catalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.1c00732?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.1c00732</a>.Stability test results of NiO-NSL (Figure S1); wide-angle XRD patterns of the as-precipitated samples using (NH4)2CO3 as the precipitant and a standard xNiCO3·yNi(OH)2 sample (Figure S2); representative TEM images of the precursors and as-calcined catalysts of the other four samples (Figures S3 and S4); specific performance data of samples in previous research (Table S1); XPS analysis of the other samples (Table S2, Figures S5 and S6); H2-TPR profiles of the other samples (Table S3, Figures S7 and S8); detailed DFT calculation results (Table S4); the surface model used in the calculations (Figure S9) (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.1c00732/suppl_file/an1c00732_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Porous NiO Nano-Sheet As an Active and Stable Catalyst for CH4 Deep Oxidation

Irregularly Shaped NiO Nanostructures for Catalytic Lean Methane Combustion

Nickel Hydroxide Nanosheets Prepared by a Direct Manual Grinding Strategy for High-Efficiency Catalytic Combustion of Methane

Catalytic Performance of Novel Hierarchical Porous Flower-Like NiCo2O4 Supported Pd in Lean Methane Oxidation

Nickel Oxide Nanoparticles on KIT-6: An Efficient Catalyst in Methane Combustion

Electron transferring with oxygen defects on Ni-promoted Pd/Al 2 O 3 catalysts for low-temperature lean methane combustion

Ni-based Catalyst Supported on Ordered Mesoporous Al2O3 for Dry CH4 Reforming: Effect of the Pore Structure

Catalytic conversion of high-GWP gases N2O and CH4 to syngas (H2 + CO) on SiO2@Ni-Cr layered nano-oxide-coated monolithic catalyst

Electron Transferring with Oxygen Defects on Ni-promoted Pd/Al2O3 Catalysts for Low-Temperature Lean Methane Combustion

Incorporating Si into NiO support to facilitate oxygen activation for CH 4 combustion

A facial strategy to synthesize Pd/Co3O4 nanosheets with enhanced performance for methane catalytic oxidation

Atomically Dispersed Nickel Anchored on a Nitrogen‐Doped Carbon/TiO2Composite for Efficient and Selective Photocatalytic CH4Oxidation to Oxygenates

NiO Nano- and Microparticles Prepared by Solvothermal Method—Amazing Catalysts for CO2 Methanation

Sub-3 Nm Pores in Two-Dimensional Nanomesh Promoting the Generation of Electroactive Phase for Robust Water Oxidation

Atomically Dispersed Nickel Anchored on a Nitrogen‐Doped Carbon/TiO2 Composite for Efficient and Selective Photocatalytic CH4 Oxidation to Oxygenates

Durable PdNi/Al2O3 Catalysts with PdO-NiO and PdO-NiAl2O4 Dual Interfaces for Methane Combustion

Enhanced water oxidation activity of 3D porous carbon by incorporation of heterogeneous Ni/NiO nanoparticles

Robust and Coke-free Ni Catalyst Stabilized by 1–2 nm-Thick Multielement Oxide for Methane Dry Reforming

Nickel phosphide nanoparticles as a noble-metal-free co-catalyst for the selective photocatalytic aerobic oxidation of CH4 into CO and H2

Porous NiCo2O4 Nanostructures As Bi-Functional Electrocatalysts for CH3OH Oxidation Reaction and H2O2 Reduction Reaction

The effect of existence states of PdOx supported by Co3O4 nanoplatelets on catalytic oxidation of methane