Abstract:Solution‐processed metal‐oxide thin films based on high dielectric constant (k) materials have been extensively studied for use in low‐cost and high‐performance thin‐film transistors (TFTs). Here, scandium oxide (ScOx) is fabricated as a TFT dielectric with excellent electrical properties using a novel water‐inducement method. The thin films are annealed at various temperatures and characterized by using X‐ray diffraction, atomic‐force microscopy, X‐ray photoelectron spectroscopy, optical spectroscopy, and a series of electrical measurements. The optimized ScOx thin film exhibits a low‐leakage current density of 0.2 nA cm−2 at 2 MV cm−1, a large areal capacitance of 460 nF cm−2 at 20 Hz and a permittivity of 12.1. To verify the possible applications of ScOx thin films as the gate dielectric in complementary metal oxide semiconductor (CMOS) electronics, they were integrated in both n‐type InZnO (IZO) and p‐type CuO TFTs for testing. The water‐induced full oxide IZO/ScOx TFTs exhibit an excellent performance, including a high electron mobility of 27.7 cm2 V−1 s−1, a large current ratio (Ion/Ioff) of 2.7 × 107 and high stability. Moreover, as far as we know it is the first time that solution‐processed p‐type oxide TFTs based on a high‐k dielectric are achieved. The as‐fabricated p‐type CuO/ScOx TFTs exhibit a large Ion/Ioff of around 105 and a hole mobility of 0.8 cm2 V−1 at an operating voltage of 3 V. To the best of our knowledge, these electrical parameters are among the highest performances for solution‐processed p‐type TFTs, which represents a great step towards the achievement of low‐cost, all‐oxide, and low‐power consumption CMOS logics.

Water‐Induced Scandium Oxide Dielectric for Low‐Operating Voltage N‐ and P‐type Metal‐Oxide Thin‐Film Transistors

Eco-Friendly, Water-Induced In2O3 Thin Films for High-Performance Thin-Film Transistors and Inverters

Fully solution-induced high performance indium oxide thin film transistors with ZrOx high-k gate dielectrics

A water-induced high- k yttrium oxide dielectric for fully-solution-processed oxide thin-film transistors

Solution-Processed High-K Magnesium Oxide Dielectrics For Low-Voltage Oxide Thin-Film Transistors

Low-temperature, High-Stability, Flexible Thin-Film Transistors with a Novel ScxIn1−xO3semiconductor

Eco-Friendly Water-Induced Aluminum Oxide Dielectrics and Their Application in A Hybrid Metal Oxide/Polymer Tft

Solution‐Processed Alkaline Lithium Oxide Dielectrics for Applications in N‐ and P‐type Thin‐Film Transistors

Low-temperature, Nontoxic Water-Induced High-K Zirconium Oxide Dielectrics for Low-Voltage, High-Performance Oxide Thin-Film Transistors

Fully solution-processed low-voltage aqueous In2O3 thin-film transistors using an ultrathin ZrO(x) dielectric.

Water-Processed Ultrathin Crystalline Indium–Boron–Oxide Channel for High-Performance Thin-Film Transistor Applications

Aqueous solution-deposited aluminum-gallium-oxide alloy gate dielectrics for low voltage fully oxide thin film transistors

A Sputtered Silicon Oxide Electrolyte for High-Performance Thin-Film Transistors

Fully Printed Top-Gate Metal–Oxide Thin-Film Transistors Based on Scandium-Zirconium-Oxide Dielectric

Solution-processed ytterbium oxide dielectrics for low-voltage thin-film transistors and inverters

Low‐Temperature, Nontoxic Water‐Induced Metal‐Oxide Thin Films and Their Application in Thin‐Film Transistors

Solution Processed Metal Oxide High-κ Dielectrics for Emerging Transistors and Circuits

Enhancement of electrical properties of solution-processed oxide thin film transistors using ZrO<sub>2</sub> gate dielectrics deposited by an oxygen-doped solution

High-mobility p-type NiOx thin-film transistors processed at low temperatures with Al2O3 high-k dielectric

High-Performance Thin-Film Transistors with Solution-Processed Scino Channel Layer Based on Environmental Friendly Precursor

P‐7.10: Facile low‐temperature solution‐processed ZrO<sub>2</sub> films as high‐k dielectrics for flexible low ‐ power thin‐film transistors