The Electrocatalytic Characterization and Mechanism of Carbon Nanotubes with Different Numbers of Walls for the VO2+/VO2+ Redox Couple.
Zhaoqian Lv,Jin Zhang,Yang Lv,Yi Cheng,San Ping Jiang,Yan Xiang,Shanfu Lu
DOI: https://doi.org/10.1039/c7cp08683k
2018-01-01
Abstract:Carbon nanotubes (CNTs) have been applied as catalysts in the VO2+/VO2+ redox, whereas the mechanism of CNTs for the redox reaction is still unclear. In this work, the mechanism of the VO2+/VO2+ redox is investigated by comparing the electrocatalytic performance of CNTs with different distributions. For different CNTs, the peak current density of the VO2+/VO2+ redox increases with increasing content of oxygen-functional groups on the surface of CNTs, especially the carboxyl group which is proved as active sites for the redox reaction. Moreover, the reversibility of the VO2+/VO2+ redox decreases with increasing defects of CNTs, as the defects affect the charge transfer of the catalytic reaction. Nevertheless, when a multi-walled CNT sample is oxidized to achieve a high content of oxygen functional groups and defects, the peak current density of the redox reaction increases from 38.5 mA mg-1 to 45.4 mA mg-1 whilst the peak potential separation (ΔEp) also increases from 0.176 V to 0.209 V. Overall, a balance between the oxygen functional groups and the defects of CNTs affects the peak current and the reversibility for the VO2+/VO2+ redox.