Hierarchical Microtubes Constructed by MoS 2 Nanosheets with Enhanced Sodium Storage Performance
Peiyuan Wang,Shumin Sun,Yu Jiang,Qiong Cai,Yong-Hui Zhang,Liming Zhou,Shaoming Fang,Jian Liu,Yan Yu
DOI: https://doi.org/10.1021/acsnano.0c06250
IF: 17.1
2020-10-27
ACS Nano
Abstract:Emerging sodium-ion batteries (SIBs) have aroused great attention in large-scale energy storage. However, it is still a great challenge to develop suitable electrode materials due to the large radius of Na<sup>+</sup>. This work demonstrates a strategy to synthesize hierarchical tubular MoS<sub>2</sub><i>via</i> a facial hydrothermal method with the assistance of tetramethylammonium bromide (TMAB). The results show that sufficient amounts of TMA<sup>+</sup> ions are necessary to form the hierarchical tubular structures of MoS<sub>2</sub>. The obtained tubular MoS<sub>2</sub> displays a high diffusion coefficient of Na<sup>+</sup> ions, a high specific capacity of 652.5 mAh/g at the current density of 100 mA/g after 50 cycles, and a good cycling stability (94.2% of the initial capacity can be retained after 100 cycles at 1000 mA/g). <i>In situ</i> XRD during the discharge/charge process displays a reversible intercalation/deintercalation of Na<sup>+</sup> into MoS<sub>2</sub> layers followed by a conversion-type reaction. Systematic analyses reveal that the enhanced electrochemical performance is attributed to its tubular hierarchical structures with the wall composed of loosely stacked nanosheets, which can provide nearly unobstructed ion transportation paths, sufficient active sites, and enough space to mitigate the effects of the volume change during the discharge/charge process. This synthetic approach can be easily extended to other metal oxides and metal sulfides with hierarchical structures for versatile applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c06250?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c06250</a>.SEM and TEM images of synthesized tubular MoS<sub>2</sub> (MS-T); XRD patterns and SEM images of MoS<sub>2</sub> synthesized with TMAC and NaBr as additives; SEM images and XRD patterns of synthesized MoS<sub>2</sub> with different TMAB concentrations; SEM images and XRD patterns of synthesized MoS<sub>2</sub> precursor with different hydrothermal treatment times; nitrogen sorption isotherms, pore size distribution curves, XPS spectra, and cyclic voltammograms at various scanning rates of MS-T, MS-S, and MS-B; contribution ratio of capacitive capacity at various scanning rates for MS-S and MS-B; Nyqust plots of electrodes MS-T, MS-S, and MS-B before and after cycling; SEM images of MS-T after cycling; XRD pattern of MS-T after complete discharge; discharge/charge curves and cyclic performance of the MS-T//Na<sub>3</sub>V<sub>2</sub>(PO<sub>4</sub>)<sub>3</sub> full cell (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c06250/suppl_file/nn0c06250_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology