Impact of the Siloxane-Terminated Side Chain on Photovoltaic Performances of the Dithienylbenzodithiophene-Difluorobenzotriazole-Based Wide Band Gap Polymer Donor in Non-Fullerene Polymer Solar Cells
Haiying Jiang,Feilong Pan,Lianjie Zhang,Xiaobo Zhou,Zhen Wang,Yaowen Nian,Gang Liu,Wei Tang,Qiao Ma,Zhenyu Ni,Mingjun Chen,Wei Ma,Yong Cao,Junwu Chen
DOI: https://doi.org/10.1021/acsami.9b08722
IF: 9.5
2019-01-01
ACS Applied Materials & Interfaces
Abstract:To thoroughly disclose the role of siloxane-terminated side chain with different substituent positions, three difluorobenzotriazole-dithienylbenzodithiophene (FTAZ-BDTT) based polymers PBZ-1Si, PBZ-2Si and PBZ-3Si with the siloxane-terminated side chain on the FTAZ unit (PBZ-1Si), on the BDTT unit (PBZ-2Si), and both on BDTT and FTAZ unit (PBZ-3Si), respectively, were synthesized. The different side chain substitutions have slight influences on absorption behavior, thermal stability, and frontier molecular orbitals, but showing great effect on the aggregation of the polymers. Grazing-incidence wide-angle X-ray scattering (GIWAXS) measurements reveal that, relative to PBZ-1Si with branched alkyl on the BDTT unit, polymers PBZ-2Si and PBZ-3Si, bearing the siloxane-terminated side chains on the BDTT unit, exhibit smaller π-π stacking distances and larger crystal coherence lengths (CL), suggesting that adopting the siloxane-terminated side chain on the BDTT unit can promote the interchain π-π interaction and the ordering of molecular packing. With IT-M as the non-fullerene acceptor, among the three polymers, the PBZ-2Si based active layer possesses the highest ordered crystals for both polymer and IT-M as well as the purest domain, which affords efficient exciton dissociation, the most balanced hole-electron transport, and reduced recombination, leading to the highest short-circuit current density (Jsc) and fill factor (FF) and then the highest power conversion efficiency (PCE) of 11.14%. In contrast, PBZ-1Si and PBZ-3Si based devices show lower PCEs of 8.98% and 9.92%, respectively. Moreover, PBZ-2Si:IT-M also exhibits good thickness tolerance and its thick active layer of 240 nm shows the most limited decreasing of efficiency after a storage for 77 days, supplying good potential for mass farbication. Our work suggests that the fine pairing of a siloxane-terminated side chain and an alkyl side chain is benifical for the opitmizing of a conjugated polymer donor towards high performance non-fullerene polymer solar cells.