Abstract:Nano-scale nickel oxide materials were prepared by solvothermal method using nickel acetylacetonate, oleic acid and oleylamine as raw materials, octadecene as solvent and polyvinylpyrrolidone as surfactant. The effects of the ratio of reactants ratio, insulation time, surfactant and the mass of oleylamine on the microstructure, particle size, morphology, optics and catalytic properties of the product were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), ultraviolet-visible spectroscopy (UV-Vis) spectral analysis, and Tafel test. The specific experimental operations were: the oleic acid (OA) and 1-octadecene (ODE) was added into four flasks (500 mL) with heating and stirring. Nickel acetylacetonate was added when the temperature raise to 50 degrees C, then continuously stirring for 60 minutes at 120 degrees C before a certain amount of oleylamine (OAm) was added to the reaction system. The mixed solution was poured into the inner liner of the high temperature reactor. The reactor was covered and transferred to the electro-thermostatic blast oven for a period of time and then cooled to room temperature. The main research results were obtained: (1) The boundary of the original particles became smoothed after sintering, and the spherical particles become flake-shaped which might be attributed to the residual organic covering so the size of nickel oxide nanoparticles changed from the original 40 similar to 45 nm to 30 similar to 40 nm. (2) With the addition of PVP, the content of NiO phase increased and the particle size was controlled within 40 similar to 45 nm. The UV-Vis test showed that NiO belonged to direct band gap and the band gap width was 3.5 similar to 3.7 eV. (3) The Tafel analysis showed that the best catalytic activity with exchange current density J(0) was 1.23x10(-2) mA,cm(-2), where pure NiO could be obtained when the reactant ratio of n[Ni(acac)(2)] : n(OA)-1: 2, the additive PVP mass fraction was of 1.66%, the amount of oleylamine was of 30 mmol, and the temperature was of 200 degrees C for 8 h.

Metallic Nickel Preparation by Electro-Deoxidation in Molten Sodium Hydroxide

Effective Anodic Sulfide Removal Catalyzed by Single Nickel Atoms on Nitrogen-Doped Graphene with Stainless Steel Substrate

RESEARCH ON PREPARATION OF NICKEL POWDER BY ELECTROLYTIC DEOXIDATION FROM NiO

Nickel Oxide/nickel Nanohybrids for Oxygen and Hydrogen Evolution in Alkaline Media

A Facile Electrochemical Lithiation Method to Prepare Porous Nickel Oxide Electrodes with High Electrochromic Performance

Preparation of Ultrafine Nickel Powder by Polyol Method and Its Oxidation Product

Preparation of Nanocrystalline NiO by Electrochemical Dissolution of Nickel

Preparation of nickel-manganese based bimetallic hydroxide nanosheets for enhanced electrocatalytic oxygen evolution reaction

Preparation and Electrochemical Properties of Nickel Oxide by Molten-Salt Synthesis

Preparation Of Nickel Foam Supported Fe2o3@Ni3s2 Nanowires Network Electrode And Electrocatalytic Oxygen Evolution Performance

Research on Influence of Electrolytic Condition in Preparation of Ni from NiO by Molten Salt Electrolysis

Preparation of Ni3Sn2 Alloy Negative Electrode for Lithium-Ion Batteries by Electro-Deoxidization in Molten Salt

High-efficiency Nickel Recovery from Spent Electroless Nickel Plating Solution: Effective Degradation of High-Concentration Nickel Complexes to Form a Nickel Ferrite Nanomaterial Via Fe3O4 Catalytic Oxidation

Electrodeposition of Bright Nickel from Liquid Ammonia Solution Containing Chloride

Solvothermal Preparation and Characterization of Nano-nickel Oxide

Preparation of Metallic Ni3N Nanoparticles and Its Electrooxidation Performance for Ethylene Glycol

High-efficiency Nickel Recovery from Spent Electroless Nickel Plating Solution: Effective Degradation of High-concentration Nickel Complexes to Form Nickel Ferrite Nanomaterial via Fe 3 O 4 Catalytic Oxidation

Outstanding Oxygen Evolution Reaction Performance of Nickel Iron Selenide/stainless Steel Mat for Water Electrolysis

Effect of Preparation Condition on Electrochemical Property of Nano-Nickel Powders

Mechanism of corrosion and sedimentation of nickel electrodes for alkaline water electrolysis

Surface Electrochemical Modification of a Nickel Substrate to Prepare a NiFe‐based Electrode for Water Oxidation