Abstract:Two kinds of fluorine-containing acrylic copolymers were prepared with an in situ radical polymerization fluorine modification method and a post-polymerization fluorine modification route, respectively. And a kind of common acrylic copolymer as the reference was synthesized. Acrylic polyurethane was prepared using the synthesized acrylic copolymers and a trimer of the hexamethylene diisocyanate curing agent. Different environments including an indoor atmospheric environment, a hygrothermal environment, a different temperature environment, as well as a xenon arc aging environment were employed to investigate the failure behavior of the coatings. Fourier transform infrared spectroscopy (FT-IR) and F-19 NMR were employed to characterize the chemical structure of the copolymers. The glass transition temperature (T-g) of the copolymers was tested using differential scanning calorimetry (DSC). The water contact angles of the coatings were monitored during the failure process. The difference in hydrophobicity of the coatings was examined. The thermostability of the coatings was explored using thermogravimetric analysis (TGA). The elemental composition of the coating surface before and after the failure experiment was analyzed using an X-ray photoelectron spectrometer (XPS). The results showed that the fluorine-containing copolymers and the corresponding hydrophobic coatings were prepared as expected. The Copolymer b coating, from the fluorine-containing acrylic copolymer prepared with the in situ polymerization fluorine modification route, exhibited better hydrophobicity in all of the above environments compared with the hydrocarbon acrylic copolymer coating (Copolymer a). The Copolymer c coating, prepared with the fluorine-containing acrylic copolymer via the post-polymerization fluorine modification method, achieved the best hydrophobicity under moderate conditions and failed quickly in hostile environments. The different fluorine modification methods resulted in different failure behaviors.

Synthesis and surface properties study of novel fluorine-containing homopolymer and copolymers for coating applications

Synthesis of fluorinated monomer and formation of hydrophobic surface therefrom

Synthesis Of Fluoroalkyl-Modified Polyester And Its Application In Improving The Hydrophobicity And Oleophobicity Of Cured Polyester Coatings

Synthesis of Fluorinated Polyester Used for Hydrophobic Coating: Influence of Fluoroalkyl Group Length on Enrichment Behavior

Study on the Synthesis and Superhydrophobic Properties of Fluorinated Copolymers with Carboxyl Group

Synthesis and characterization of fluorine-containing polyester based on phthalic anhydride and tetrafluoropropyl glycidyl ether

SYNTHESIS AND PRELIMINARY PROPERTIES OF A WATER-REPELLENT POLY(ARYLENE ETHER)

Study on Synthesis of Fluorinated Acrylate Copolymer and Surface Hydro-Oleophobic Properties of the Copolymer Films

Study on Crystallization and Surface Properties of Fluorinated Acrylate Copolymers

Preparation Of Fluoro-Modified Acrylate Copolymer And Hydrophobicity Of Coatings Therefrom

Preparation and Characterization of Copolymer Containing Fluorine-Silicon with Low Surface Energy

Research of Fluorine-Modified Two Component Waterborne Acrylic Polyurethane Coating Performance

Synthesis and surface property characterization of polyacrylate with short fluorocarbon side chain

Novel Fluorinated Polymers Containing Short Perfluorobutyl Side Chains and Their Super Wetting Performance on Diverse Substrates

Preparation and hydrophobicity failure behavior of two kinds of fluorine-containing acrylic polyurethane coatings

Higher Water Repellency Caused by a Reduced Employment of Low Surface Energy Structures

Crystalline Alkyl Side Chain Enhanced Hydrophobicity–Oleophobicity for Transparent and Durable Low-Surface-Energy Coatings Based on Short Fluorinated Copolymers

RESEARCH PROGRESS IN FLUORINE-CONTAINING ACRYLATE POLYMER

Synthesis and Characterization of Hybrid Fluoro‐emulsion Based on Silica/copolymer Composite Particles

SYNTHESIS AND CHARACTERIZATION OF DIBLOCK COPOLYMER OF BUTYL METHACRYLATE AND PERFLUOROALKYL ACRYLATE

Novel linear fluoro-silicon-containing pentablock copolymers: Synthesis and their properties as coating materials