Abstract:This study addressed different materials to coat iron oxide, after using co-precipitation to synthesize. During synthesizing iron oxide, FeSO4•7H2O as a single raw material , was emphasized as a precursor salt. In advance, FeSO4•7H2O was oxidized into trivalence by using hydrogen peroxide, allocated Fe(Ⅱ)and Fe(Ⅲ) mole ratio as one to two, and synthesized ferric ferrous oxide nanoparticle by sodium hydroxide co-precipitation, which TX-100 was a protective agent to disperse uniformly. Depend on the morphology of several nanopartical types through the processing, separation of precursor salt solution and NaOH solution in pump by adding TX-100 solution would get Fe3O4 ratio more evenly. Besides during the experiment, variety loading of NaOH and dispersant, using two- stage method to add NaOH as well, rod and particle mixure would obtain. XRD, SQUID, HRTEM and SEM were used to analyze the particle size, uniformity, Magnetic, and Crystal structure. Also, intend to find the relation among synthesis and properties, and continue to work on electrodes for battery application to seek the optimal performance corresponded to synthesis conditions. Preparation of Fe3O4@Ag was took AgNO3 and C6H12O6, the reductant, into Fe3O4 solution. Different mole ratio of AgNO3 and Fe3O4 were mix- coated. Through the process, surface modifier makes coating completely and uniformly. Later, same analysis entailed to Fe3O4@Ag product powder. The purpose was to examine its completely coating, thickness, and magnetism.

Green synthesis and surface properties of Fe 3 O 4 @SA core–shell nanocomposites

Preparation, characterization, and catalytic activity of core/shell Fe3O4@polyaniline@au nanocomposites.

Green Synthesis, Characterization and Application of Proanthocyanidins-Functionalized Fe3O4 Magnetic Nanocomposites

Effects of Boards of Directors' External Ties on IT Assimilation

Green Synthesis, Characterization and Application of Proanthocyanidins-Functionalized Fe<sub>3</sub>O<sub>4</sub> Magnetic Nanocomposites

Facile green synthesis of core–shell magnetic MOF composites (Fe3O4@SiO2@HKUST-1) for enhanced adsorption capacity of methylene blue

Synthesis, Surface Modification and Characterization of Magnetic Fe3O4@SiO2 Core-Shell Nanoparticles

Superparamagnetic Ag@Fe3o4 Core-Shell Nanospheres: Fabrication, Characterization And Application As Reusable Nanocatalysts

Fabrication of Fe3O4@APF Magnetic Nanospheres with Tunable Core–Shell Structure: An Effective Carrier and Reducing Agent for Ag Nanoparticles

Fabrication of Magnetic Core–shell Nanocomposites with Superior Performance for Water Treatment

Preparation, Surface Functionalization and Application of Fe3O4 Magnetic Nanoparticles

Facile Preparation of Superparamagnetic Fe3O4/poly(St-co-MPS)/SiO2 Composite Particles with High Magnetization by Introduction of Silanol Groups.

Green Synthesis of Pure Superparamagnetic Fe3O4 Nanoparticles Using Shewanella sp. in a Non-Growth Medium

Study on the Synthesis and Application of Core-Shell Structured Nanoparticles of Fe3O4

Synthesis of Fe3O4@Polyaniline Core/Shell Microspheres with Well-Defined Blackberry-Like Morphology

Preparation and Potential Applications of Super Paramagnetic Nano-Fe3O4

Synthesis, characterization, and electrochemical applications of multifunctional Fe 3 O 4 @C–Au nanocomposites

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Size-controlled synthesis of Fe3O4 and Fe3O4@SiO2 nanoparticles and their superparamagnetic properties tailoring

A Simple Synthesis of Fe3O4 Nanoclusters and Their Electromagnetic Nanocomposites with Polyaniline

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties