Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Hydrothermal preparation of WO3 nanorod array and ZnO nanosheet array composite structures on FTO substrates with enhanced photocatalytic properties

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Effect of UV irradiation on the properties of ZnO nanorod arrays prepared by hydrothermal method

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

A Facile Method to Fabricate Superhydrophobic ZnO Nanostructure with Petal Effect

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Conformal growth of ZnO on TiO2 nanowire array for enhanced photocatalytic activity

Novel Route to WO<i><sub>x</sub></i>Nanorods and WS<sub>2</sub>Nanotubes from WS<sub>2</sub>Inorganic Fullerenes

Preparation of microstructured ZnO nanorod photoelectrode

Novel route to WOx nanorods and WS2 nanotubes from WS2 inorganic fullerenes.

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Controllable Preparation and Photocatalytic Activity of Highly Ordered ZnO Nanoarrays

Fabrication and Morphology of ZnO Nanorods Array Prepared from Aqueous Solution under an Assisted Electrical Field

Piezoelectric potential enhanced photocatalytic performance based on ZnO with different nanostructures

Nanofiber template-induced preparation of ZnO nanocrystal and its application in photocatalysis

Hierarchical Assembly of SnO 2 /ZnO Nanostructures for Enhanced Photocatalytic Performance

Controlled Synthesis Of The Znwo4 Nanostructure And Effects On The Photocatalytic Performance

Structure Transformation of Hydrothermally Treated ZnO Nanorod Array

Synthesis of ZnWO4 nanorods with [100] orientation and enhanced photocatalytic properties

Hydrothermal Growth of ZnO Nanowire Arrays: Fine Tuning by Precursor Supersaturation