Energy Storage Properties of BNT-BT Based Solid Solution

Qi Xu,Hanxing Liu,Lin Zhang,Minghe Cao,Juan Xie,Hua Hao,Zhonghua Yao
DOI: https://doi.org/10.1109/isaf.2015.7172675
2015-01-01
Abstract:The phase structure, microstructure, dielectric and energy storage properties of 0.85(0.92Bi0.5Na0.5TiO3-0.08BaTiO3)-0.15(Na1-3xBixNbO3) (BNTBT-NBxN) polycrystalline lead-free ceramics were systematically investigated. Dense and pore-free samples were prepared by conventional solid state reaction method. X-ray diffraction results indicated that the solid solubility of Bi in BNTBT-NBxN system lay at x=0.05~0.07. Within the solid solubility, the first dielectric anomaly which located at temperature Ts was depressed and shifted towards lower temperature with x increasing. As a consequence, the temperature stability of dielectric properties was largely improved, which demonstrated that BNTBT-NBxN ceramics were promising for high-temperature capacitor dielectrics. The ferroelectric properties analysis indicated that with the increase of x, the maximum polarization Pm gradually reduced and the P-E loops became slant and slim. The optimum energy storage properties was obtained for x=0.05 with energy storage density W=1.29J/cm3 and energy storage efficiency η=76%.
What problem does this paper attempt to address?