Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides
Zihao Zhang,Shize Yang,Xiaobing Hu,Haidi Xu,Hanggen Peng,Miaomiao Liu,Bishnu Prasad Thapaliya,Kecheng Jie,Jiahua Zhao,Jixing Liu,Hao Chen,Yan Leng,Xiuyang Lu,Jie Fu,Pengfei Zhang,Sheng Dai
DOI: https://doi.org/10.1021/acs.chemmater.9b01244
IF: 10.508
2019-01-01
Chemistry of Materials
Abstract:Mesoporous metal oxides with wide pore size, high surface area, and uniform porous structures have demonstrated excellent advantages in various fields. However, the state-of-art synthesis approaches are dominated by wet chemistry, accompanied by use of excessive solvent, and the requirement of time-consuming drying process. Herein, we report a mechanochemical solid-state route to synthesize mesoporous Al2O3 (meso-Al2O3) via aluminum isopropoxide-copolymers assembly. The obtained meso-Al2O3 shows a record high surface area (similar to 644 m(2) g(-1)) and narrow pore size distribution (centered at similar to 5 nm). Moreover, a mechanochemical nonhydrolytic sol-gel strategy is introduced to fabricate mesoporous metal (Cu, Co, Mn, Fe, Mg, Ni)-aluminum binary oxide by using anhydrous metal chlorides and aluminum isopropoxide interplay. More importantly, four or five metals-aluminum oxide complexes with abundant mesopores and single cubic crystalline phase known as high-entropy ceramics are produced. To the best of our knowledge, mesoporous high-entropy metal oxides have not been prepared before, because the high crystallization temperature would make mesopores collapse. Additionally, this high-entropy property endows (CuNiFeCoMg)O-x-Al2O3 with superior SO2-resisting performance (1000 ppm of SO2 in N-2 at 280 degrees C) in the catalytic oxidation of CO compared to single CuO-Al2O3.