Abstract:A kind of hydrophobic silica with good dispersibility was prepared first. The silica and epoxy natural rubber (ENR) were blended in Haake internal mixer at high temperature in a powerful shear force filed, and so the grafted silica was made through in-situ grafting reaction between the hydroxyl groups of silica and the epoxy groups of ENR. The grafting processes were performed as follows: first, the silica should be dried about 24 h at 100 degrees C in an oven to remove the free water molecules that absorbed on the surface of silica. Secondly, the grafting reaction temperature was chosen at 170 degrees C that confirmed by the test result of a Monsanto MDR-2000 moving die rheometer, and the weight proportions between silica and ENR were chosen to be 1: 1, 2: 1 and 3: 1 separately in this study. Thirdly, ENR was mixed in HAAKE internal mixer about I min, then silica was added to react with the ENR for another 15 min before discharged, and the outputs named ENR-grafted silica were obtained as we wanted. In order to obtain an appropriate grafting condition, the effect of different weight proportions between silica and ENR on the stress-strain curves of natural rubber composites reinforced by the grafted silica was discussed. Through analyses of the reinforcement effect, the appropriate proportion between silica and ENR was chosen to be 3: 1. FTIR, TGA and TEM analysis results indicated that ENR was successfully grafted onto the silica surface. FTIR result of the grafted silica showed the new absorptions. The peaks at 2966,2929 and 2862 cm(-1) are assigned to CH stretching vibrations. The absorption band at 1660 cm(-1) is characteristic of C C stretching. The stretching vibration of epoxy groups that should be at 870 cm-' was missing, suggesting the epoxy groups were almost used up to react with silanol groups. A new shoulder peak appears at 3640 cm(-1), which is ascribed to - 011 stretching of C-OH which is the result of the reaction of silanol groups and ENR. TGA curves revealed ENR grafted silica showed a new step between 348 - 449 degrees C due to the decomposition of ENR, and the grafting rate reached 21.3 %. TEM images indicated the size of silica agglomerates became small obviously after modification because of the grafting layer preventing the silica particles from conglomerating. Then, compared with the silica without grafting, the properties of NR composites filled with grafted silica were investigated. The "Payne effect" results indicated that the grafted ENR molecules reduced the silica-silica interaction by enhancing the rubber-silica interaction, and so the grafted silica had better dispersibility in natural rubber ( NR) composites. Mechanical properties test of NR composites proved that the grafted silica could more effectively improve the reinforcement effect due to the strong interface combination between silica and ENR. DMA results showed that the temperature of glassy transition of ENR bound to the silica surface shifted to higher temperatures. Consequently, the composite contained the grafted silica had high strength and high hysteresis at the same time on the normal temperature. So the composites have potential application in the shocking absorber products, the tire of racing cars, and so on.

The grafting reaction of epoxidized natural rubber with carboxyl ionic liquids and the ionic conductivity of solid electrolyte composites

Grafting modification of epoxidized natural rubber with poly(ethylene glycol) monomethylether carboxylic acid and ionic conductivity of graft polymer composite electrolytes

The Grafting Reaction of Epoxycyclohexyl Polyhedral Oligomeric Silsesquioxanes with Carboxylic Methoxypolyethylene Glycols and the Properties of Composite Solid Polymer Electrolytes with the Graftomer

Studies on Conductivity of Acrylonitrile‐butadiene Rubber/liclo4 Composite and Its Modification by Adding Epoxy Resin

Preparation and proton conductivity of poly(vinylidene fluoride)/layered double hydroxide nanocomposite gel electrolytes

Influence of Grafting Modification on Dielectric Properties of Epoxy-Grafted SiO2/Epoxy Composites

Improved Ionic Conductivity of Nbr/Epoxy Resin/Liclo4 Composites by Adding Ionic Liquid

Molecular Dynamics Simulations on Epoxy Resin Composite via Grafting Acryloyl-chloride to Inhibit Electron Transport and Improve Thermal-mechanical Properties

Complementary Hybrid Design of Solvated Electrolyte Membranes Enabled by Porous Carbon Reinforcement for High-Performance Lithium Batteries

In situ Grafting onto Silica Surface with Epoxidized Natural Rubber via Solid State Method

Study on Preparation and Properties of Gel Polymer Electrolytes Based on Comb-Like Copolymer Matrix of Poly(ethylene Glycol) Monomethylether Grafted Carboxylated Butadiene-Acrylonitrile Rubber

Conductive epoxidized natural rubber nanocomposite with mechanical and electrical performance boosted by hybrid network structures

Influence of binary lithium salts on 49% poly(methyl methacrylate) grafted natural rubber based solid polymer electrolytes

Highly Conductive Polymer Composites from Room-Temperature Ionic Liquid Cured Epoxy Resin: Effect of Interphase Layer on Percolation Conductance

Hybrid Alumina–Silica Filler for Thermally Conductive Epoxidized Natural Rubber

PREPARATION AND CHARACTERIZATION OF THE NATURAL RUBBER COMPOSITES REINFORCED BY EPOXY NATURAL RUBBER GRAFTED SILICA WITH GOOD DISPERSIBILITY

Synthesis and ionic conductivity of model graft polyether network electrolyte

Synthesis, structure and electrochemical characterization, and dynamic properties of double core branched organic–inorganic hybrid electrolyte membranes

Achieving High Anion Conductivity by Densely Grafting of Ionic Strings

Mechanical, Dielectric and Actuated Properties of Carboxyl Grafted Silicone Elastomer Composites Containing Epoxy-Functionalized TiO2 Filler

Synthesis and Characterization of Novel Crosslinked Polyurethane–acrylate Electrolyte