Abstract:Without use of any templates or shape-protectors, uniformly sized anatase TiO2 nanocrystallites with cuboidal morphology were synthesized by changing titanium hydroxide precipitates into their corresponding ethanol-gels (viz. by washing several times with anhydrous ethanol) followed by drying in supercritical ethanol (7.0MPa, 270°C) and calcination at high temperature (AS-preparation). Characterizations with X-ray diffraction (XRD), Raman spectroscopy and nitrogen adsorption suggest that the cuboidal anatase nanocrystallites are highly resistant to thermal sintering. The anatase structure of the cuboidal nanocrystallites was maintained even after calcinations up to temperatures as high as 800°C. Thermogravimetric (TG) measurements in flowing air show that the as-prepared cuboidal TiO2 nanocrystallites were contaminated with some carbonaceous residues, which can be completely removed by calcination at 500°C in air. Application of these cuboidal TiO2 nanocrystallites as photocatalytic materials was evaluated by photocatalytic degradation of methyl orange in water. With increasing the calcination temperature up to 800°C, the photocatalytic activities of anatase TiO2 cuboids increased gradually due to improved crystallization of the material. The sample calcined at 800°C afforded the highest photocatalytic activity, which is comparable to that of the commercial photocatalyst Degussa P-25. Due to the presence of carbonaceous residues after the supercritical drying in the preparation, the samples calcined at temperatures no higher than 400°C showed higher photocatalytic activities than the sample calcined at 500°C. However, further calcination of the sample at 1000°C led to drastic reduction in the photocatalytic activity due to the anatase-to-rutile phase transformation and sintering of the material.

Ionic Liquid-Assisted Synthesis of Anatase Tio2 Nanotubes and Their Uv Light Photocatalytic Activities

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

One-pot Hydrothermal Synthesis of the Dual-Phase Anatase/tio2-B Nanoparticles with K2Ti6O13 Nanofibers for Enhanced Photocatalysis

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Visible Light-Driven Iodine-Doped Titanium Dioxide Nanotubes Prepared by Hydrothermal Process and Post-Calcination

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Low Temperature Synthesis of Few-Layer Titanate Nanobelts on Ti Mesh and the Hot-Water Induced Transformations to Highly Photocatalytic Active Titania Nanorods

Characterization, Properties and Catalytic Application of TiO2 Nanotubes Prepared by Ultrasonic-Assisted Sol-Hydrothermal Method

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Titania Nanoflowers with High Photocatalytic Activity

Hydrothermal synthesis and photocatalytic property of CaTiO 3 assisted with sodium citrate

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Nonaqueous sol–gel synthesis and growth mechanism of single crystalline TiO2 nanorods with high photocatalytic activity

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Facile Synthesis of Anatase–Rutile Diphase N-doped TiO2 Nanoparticles with Excellent Visible Light Photocatalytic Activity

Effect of annealing temperature on morphology, structure and photocatalytic behavior of nanotubed H2Ti2O4(OH)2

Preparation and characterization of titanium oxide nanotubes