Influence of TiC contents on the microstructure, mechanical properties, and oxidation behavior of Mo–10Si–8B alloys
Xiancong Chen,Yakang Kong,Yi Qu,Jiabo Yu,Yilei Xiao,Cheng Wang
DOI: https://doi.org/10.1016/j.intermet.2023.108122
IF: 4.075
2023-11-22
Intermetallics
Abstract:The microstructure, mechanical properties , and oxidation behavior of Mo–10Si–8B- x TiC (at.%, x = 0,5,10,15) alloys fabricated via oscillatory pressure sintering are studied. The phase constitution of three TiC-added alloys is α-Mo + Mo 3 Si + Mo 5 SiB 2 + Mo 2 C + TiC; in 15TiC alloy α-Mo phase no longer maintains its contiguity as in the other three alloys. With further TiC addition, the microhardness improves by 60–90 % (up to 1500 HV), Young's elastic modulus increases from 328 to 368 GPa, and the fracture toughness decreases from 14.23 to 10.8 MPa m 1/2 , accounting for the less-ductile phase and newly introduced brittle phases. Thermogravimetric analysis indicates that the addition of TiC reduces the oxidation resistance. For isothermal oxidation at 800, 1000, and 1200 °C, the serious oxidation occurs for all TiC-added alloys except for 15TiC alloy at 1200 °C because the oxidation sequence changes to TiC → Mo 5 SiB 2 → Mo 3 Si → α-Mo. The anomalous phenomenon for 15TiC alloy at 1200 °C could be attributed to the rapid formation and cover of protective SiO 2 –TiO 2 layer on alloy surface after the transient MoO 3 volatilization.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering