Reinforced conducting hydrogels prepared from the in situ polymerization of aniline in an aqueous solution of sodium alginate

huabo huang,xiaoping zeng,wan li,hong wang,qin wang,yajiang yang

DOI: https://doi.org/10.1039/c4ta03332a

IF: 11.9

2014-01-01

Journal of Materials Chemistry A

Abstract:By using the in situ polymerization of aniline in an aqueous solution of sodium alginate, we prepared reinforced conducting hydrogels (PANI-SA) with good conductivity (similar to 10(-3) S cm(-1)). SEM images indicated that the microstructure of PANI-SA hydrogels was a typical 3D nano-fiber network formed by the entanglement of the PANI and SA molecular chains, leading to a good compressive strength (similar to 41 kPa). Because the system does not contain any adhesives and conducting filters, the PANI-SA conducting hydrogels with self-supported structures can be directly employed as electrode materials for supercapacitors. A study of cyclic voltammograms indicated that the currents of the cathodic peak significantly increased with an increase in the scan rate, indicating that the electrode materials possess good responsiveness. As a reference, traditional compressive tablet electrodes were also prepared by mixing the powder of PAN 1-SA xerogels, adhesive and conducting filler. The results of galvanostatic charge/discharge and impedance show that PAN 1-SA hydrogels possess longer discharge times, higher specific capacitance and lower electronic resistance in comparison with compressive tablet electrodes. After 1000 cycles of charge/discharge, there is almost no difference in the retained specific capacitance between PANI-SA hydrogels electrodes and compressive tablet electrodes. The easily fabricated PANI-SA conducting hydrogels show great potential as electrode materials for supercapacitors.