Preparation And Performance Of Wave Absorbing Materials By Metallization Of Nocadia

Han Yu,Li Songmei,Liu Jianhua,Yu Mei
2011-01-01
Acta Chimica Sinica
Abstract:Micro/nano Ni-Fe-P wave absorbing materials were prepared on the surface of Nocadia pretreated by electroless plating technique. The morphology, component, structure and magnetic property were characterized by SEM (scanning electron microscope), EDS (energy dispersive spectrometer), XRD (X-ray diffraction) and VSM (vibrating sample magnetometer). The results clearly demonstrated that one-step method was in a condition to deposit on the surface of Nocadia, and the surface of plating was roughed with the increase of the spherical particles and decomposition products due to the effects of the load, the quality of plating and the utilization of electroless solution were the best when the load was 80 mL. The average contents of Ni, Fe and P element of the metal layer with 80 mL load (w) were about 83.17%, 6.12% and 10.71%, respectively. The magnetic property was changed little by increasing of the load, and the plating was amorphous. The electromagnetic parameters were measured by VNA (vector network analyzer), the results showed that the reflection loss could reach 27 dB at the frequency of 10 similar to 12 and 15 similar to 17 GHz when the thickness was 2 mm.
What problem does this paper attempt to address?