Abstract:Magnesium alloys are potentially attractive biodegradable materials. However, their rapid corrosion rate limits their biomedical application. To slow down the rate of biodegradation, a protective calcium-phosphate coating was formed on a magnesium alloy substrate by a hydrothermal method. Scanning electron microscope results showed that the coating consisted of two layers with different crystalline characteristics. The loose outer layer showed a prism-like crystal structure, while the compact inner layer is a dense ultra-fine regular di-pyramid-like structure with an average grain dimension of ∼200 nm. The compositions of the inner layer and outer layer were calcium-deficient hydroxyapatite (Ca-def HA) and dicalcium phosphate (DCPa), respectively. The coating adhered well to the substrate with a thickness of about 15 μm. Immersion in Hank’s solution indicated that the coating could significantly improve the degradation properties of magnesium alloy. The pH of the solution containing the coated samples increased much more slowly than the untreated control. After 8 d immersion, the uncoated sample had corroded seriously while the coated sample was much less corroded. The Ca/P atom ratio in both the layers of the coating increased and the coating was still protecting the substrate. The two layers of the coating corroded differently because of differences in solubility. The outer layer was more severely attacked and many holes were formed on the surface, the inner layer suffered less attack. In addition, a growth of precipitate on the inner layer was observed, indicating that surface bioactivity was improved by the coating. Thus, magnesium alloys coated with a Ca-P coating prepared by a hydrothermal method are promising candidate biodegradable biomaterials, and further investigation of in vivo degradation behavior is suggested.

Biocorrosion Resistance of Coated Magnesium Alloy by Microarc Oxidation in Electrolyte Containing Zirconium and Calcium Salts

Micro-arc Oxidation Behaviors of AZ91D Magnesium Alloy in Different Electrolytes

Corrosion resistance of ZrO 2 –Zr-coated biodegradable surgical magnesium alloy

Corrosion Behavior of Zrn/Zr Coated Biomedical Az91 Magnesium Alloy

Degradation Behavior Of Micro-Arc Oxidized Zk60 Magnesium Alloy In A Simulated Body Fluid

Preparing Ca-P Coating on Biodegradable Magnesium Alloy by Hydrothermal Method: in Vitro Degradation Behavior

Corrosion Resistance and Surface Biocompatibility of a Microarc Oxidation Coating on a Mg–Ca Alloy

The Effects of Temperature and Gibberellic Acid on Germination of Eranthis hyemalis (L.) Salisb. seeds

Electrochemical Behavior Al[sub 2]o[sub 3]∕al Coated Surgical AZ91 Magnesium Alloy in Simulated Body Fluids

Optimization of the in Vitro Biodegradability, Cytocompatibility, and Wear Resistance of the AZ31B Alloy by Micro-Arc Oxidation Coatings Doped with Zinc Phosphate

Biodegradation Behavior of Micro-Arc Oxidation Coating on Magnesium Alloy-from a Protein Perspective

Preparation and Degradation Behavior of Composite Bio-Coating on ZK60 Magnesium Alloy Using Combined Micro-Arc Oxidation and Electrophoresis Deposition

Neuropathic pain inhibitor, RAP-103, is a potent inhibitor of microglial CCL1/CCR8

Corrosion Resistance and Cytocompatibility of Biodegradable Surgical Magnesium Alloy Coated with Hydrogenated Amorphous Silicon.

In Vitro Corrosion Behavior of Zr-Containing MAO-PLA Composite Coating on Magnesium Alloy

Biodegradable Magnesium Bone Implants Coated with a Novel Bioceramic Nanocomposite

Corrosion resistance enhanced by an atomic layer deposited Al2O3 /micro-arc oxidation coating on magnesium alloy AZ31

Surface Engineering of Biodegradable Magnesium Alloys for Enhanced Orthopedic Implants.

In Vitro Corrosion and Cytocompatibility of A Microarc Oxidation Coating and Poly(L-Lactic Acid) Composite Coating on Mg-1li-1ca Alloy for Orthopedic Implants

Fabrication and Characterization of Micro-arc Oxidation (MAO) Coatings on Novel Biodegradable Mg-1Ca Alloy for Orthopaedic Application

Effect of ZrSiO4 Concentration on the Microstructure and Corrosion Resistance of MAO Coatings Formed on AZ91 Magnesium Alloy